SABIC Innovative Plastics Cycoloy® FXC630SK PC+ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® FXC630SK PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Color package may affect performance. PC+ABS, ECO-conforming flame retardant with diamond sparkle appearance.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm

@Thickness 3.20 mm
 0.0030 - 0.0050 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 13.5 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 13.5 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 ASTM D1238
Melt Index of Compound 14 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 14 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa
6530 psi
50 mm/min; ISO 527
46.0 MPa
6670 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 59.0 MPa
8560 psi
Type I, 50 mm/min; ASTM D638
60.0 MPa
8700 psi
50 mm/min; ISO 527
Elongation at Break 7.0 %
7.0 %
50 mm/min; ISO 527
20 %
20 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 3.0 %
3.0 %
50 mm/min; ISO 527
4.0 %
4.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.80 GPa
406 ksi
1 mm/min; ISO 527
3.10 GPa
450 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 90.0 MPa
13100 psi
2 mm/min; ISO 178
94.0 MPa
13600 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.60 GPa
377 ksi
2 mm/min; ISO 178
2.68 GPa
389 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 2.13 J/cm
3.99 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 14.0 kJ/m²
6.66 ft-lb/in²
80*10*4; ISO 180/1A
Dart Drop, Total Energy 47.0 J

@Temperature 23.0 °C
 34.7 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 40.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 40.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C

@Thickness 3.20 mm
 194 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 82.0 °C

@Thickness 3.20 mm
 180 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 95.0 °C
203 °F
Rate B/120; ISO 306
98.0 °C
208 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 V-2

@Thickness 1.01 mm
 V-2

@Thickness 0.0398 in
 UL 94
V-1

@Thickness 1.19 mm
 V-1

@Thickness 0.0469 in
 UL 94
V-0

@Thickness 1.49 mm
 V-0

@Thickness 0.0587 in
 UL 94
5VB

@Thickness 2.00 mm
 5VB

@Thickness 0.0787 in
 UL 94