- HOME
- POLYMER SEARCH
- Thermoplastic
- Polyester, TP
- Polybutylene Terephthalate (PBT)
- PolyOne Lubri-Tech™ PS-15GF/10T Polybutylene Terephthalate (PBT), Glass Filled, PTFE Lubricated (discontinued
PolyOne Lubri-Tech™ PS-15GF/10T Polybutylene Terephthalate (PBT), Glass Filled, PTFE Lubricated (discontinued
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ PS-15GF/10T Polybutylene Terephthalate (PBT), Glass Filled, PTFE Lubricated
(discontinued.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedPTFE LubricatedUL 94 HB (HEM TEST)PolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 |
| Water Absorption | 0.070 % | 0.070 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0050 cm/cm | 0.0040 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 89.6 MPa | 13000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 4.83 GPa | 700 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
| Compressive Strength | 62.1 MPa | 9000 psi | ASTM D695 |
| Izod Impact, Notched | 0.534 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.00 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | Annealed, 0.125 in bars; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 243 - 266 °C | 470 - 510 °F | Molding |
| Mold Temperature | 93.3 - 121 °C | 200 - 250 °F | |
| Drying Temperature | 107 °C | 225 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Lanxess Pocan® T 7331 POS151 700226 PBT + PET, 30% Glass Fiber
- Special Metals UDIMET® Alloy 250 Maraging Steel
- Shin-Etsu Silicones KE-7021U Temperature Resistant Silicone Elastomer
- DuPont Elvaloy® 3117 AC Ethylene and 17% Butyl Acrylate Copolymer
- Dow Corning JCR 6122
- Chosun Refractories BTB-165 Casting Block
- Dow SiLK™ I 820 Semiconductor Dielectric Resin
- Bulk Molding Compounds BMC 845 30% Glass Filled Vinyl Ester
- Carpenter Custom 450® Stainless Steel, Condition H900 (Age Hardened 482°C)
- Lanxess Pocan® BFN 4231 000000 PBT, 25% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved