Category | Polymer , Thermoplastic , ABS Polymer |
Manufacturer | SABIC Innovative Plastics (GE Plastics) |
Trade Name | Cycolac® |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | SABIC Innovative Plastics Cycolac® MG38 ABS.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
Viscosity | 245000 cP | 245000 cP | Melt Viscosity, 240°C, 1000 sec-1; ASTM D3825 |
Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
Melt Flow | 3.7 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.7 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
15 g/10 min @Load 10.0 kg, Temperature 220 °C |
15 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 |
33.0 MPa | 4790 psi | 50 mm/min; ISO 527 | |
Tensile Strength, Yield | 44.0 MPa | 6380 psi | Type I, 5 mm/min; ASTM D638 |
46.0 MPa | 6670 psi | 50 mm/min; ISO 527 | |
Elongation at Break | 26 % | 26 % | Type I, 5 mm/min; ASTM D638 |
41.6 % | 41.6 % | 50 mm/min; ISO 527 | |
Elongation at Yield | 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 |
2.7 % | 2.7 % | 50 mm/min; ISO 527 | |
Tensile Modulus | 2.27 GPa | 329 ksi | 5 mm/min; ASTM D638 |
Flexural Yield Strength | 72.0 MPa | 10400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
Flexural Modulus | 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
Izod Impact, Notched | 3.73 J/cm | 6.99 ft-lb/in | ASTM D256 |
Izod Impact, Notched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | 80*10*4; ISO 180/1A |
9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
Charpy Impact, Notched | 2.90 J/cm² | 13.8 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
Dart Drop, Total Energy | 31.0 J @Temperature 23.0 °C |
22.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 88.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
CTE, linear, Transverse to Flow | 86.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
48.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C | 178 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
82.0 °C @Thickness 3.20 mm |
180 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
Vicat Softening Point | 97.0 °C | 207 °F | Rate B/50; ISO 306 |
98.0 °C | 208 °F | Rate B/50; ASTM D1525 | |
99.0 °C | 210 °F | Rate B/120; ISO 306 | |
UL RTI, Electrical | 60.0 °C | 140 °F | UL 746B |
UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | UL 746B |
UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | UL 746B |
Flammability, UL94 | HB @Thickness 1.52 mm |
HB @Thickness 0.0598 in |
UL 94 |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
Comparative Tracking Index | >= 600 V | >= 600 V | UL 746A |
Hot Wire Ignition, HWI | 15 - 30 sec | 15 - 30 sec | UL 746A |
High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A |