- RheTech Products T30P100-00 30% Talc Reinforced Polypropylene, Natural
RheTech Products T30P100-00 30% Talc Reinforced Polypropylene, Natural
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products T30P100-00 30% Talc Reinforced Polypropylene, Natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Headlamp housingsI/P componentsHVAC ductworkInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 30 % | 30 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0105 cm/cm | 0.0105 in/in | ASTM D955 |
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 230 °C |
17 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 75 | 75 | ASTM D2240 |
| Tensile Strength at Break | 27.6 MPa | 4000 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 2.90 GPa | 420 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Temperature 23.0 °C |
0.500 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 0.790 J | 0.583 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 126 °C | 258 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C | 160 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Middle Barrel Temperature | 210 - 238 °C | 410 - 460 °F | |
| Front Barrel Temperature | 216 - 243 °C | 420 - 470 °F | |
| Nozzle Temperature | 221 - 232 °C | 430 - 450 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 55.2 - 103 MPa | 8000 - 15000 psi | |
| Hold Pressure | 27.6 - 51.7 MPa | 4000 - 7500 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers AvaSpire® AV-750 GF40 Polyaryletherketone (PAEK) (Unverified Data**)
- Hong Kun Group 3-Chloro-2-fluorobenzaldehyde Pharmaceutical Intermediate
- Lord Adhesives 19 Mix-In Accelerator for 200, 400, 500 Series
- SABIC Innovative Plastics LNP THERMOCOMP C1000XXP PS (Europe-Africa-Middle East)
- Solvay ALBRITECT® CP 30 Vinyl phosphonic acid - acrylic acid copolymer, 20% Aqueous solution
- Solvay Specialty Polymers Amodel® A-8940 HS Polyphthalamide (PPA), 40% Glass Fiber
- Borealis Borecene™ RM7402 Linear Polyethylene for Rotational Molding
- Borealis Borseal™ TD110BF Terpolymer for BOPP Film
- A. Schulman CP80-01 Linear Low-Density Polyethylene
- DuPont Teijin Films Melinex® ST506 Polyester Film, 500 Gauge
Copyright © lookpolymers.com All Rights Reserved