Arlon 0.008" (0.2032 mm) Primerless Thermabond® Uncured Silicone (99990A008)

Category	Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone , Silicone Elastomer, for Thermal Management
Manufacturer	Arlon
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 0.008" (0.2032 mm) Primerless Thermabond® Uncured Silicone (99990A008).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

0.008 in., ±0.001 (0.2 mm, ±0.03) uncured silicone on 0.003 in. (0.08 mm) nominal PTFE coated fiberglass; 0.001 in. (0.03 mm) FEP interleave; overall thickness 0.008 in ±0.001(0.2 mm ± 0.03). The shelf life is defined as the duration of time for which the product will meet the physical requirements outlined below. It does not guarantee the product’s usefulness in all applications. Color: Light blue. Weight: 305.2 g/m² ± 33.9 (9.0 oz./yd.² ± 1.0). Shelf Life: 3 months from date of manufacture at 7.2°C(45°F). Thermal Impendence is 0.7°C/W, ±0.07 °C/W.Information provided by the manufacturer, Arlon Silicone Technologies Division.

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	>= 60	>= 60
Tensile Strength, Ultimate	4.68 - 5.72 MPa	679 - 830 psi
Elongation at Break	250 - 300 %	250 - 300 %
Shear Modulus	<= 0.000700 GPa	<= 0.102 ksi
Adhesive Bond Strength	>= 2.80 MPa	>= 406 psi	lap shear strength

Thermal Properties	Metric	English
Thermal Conductivity	0.280 - 0.360 W/m-K	1.94 - 2.50 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air	232 °C	450 °F
Minimum Service Temperature, Air	-73.3 °C	-99.9 °F

Electrical Properties	Metric	English	Comments
Dielectric Strength	14.0 kV/mm	356 kV/in	2.8 kV minimum

Processing Properties	Metric	English	Comments
Processing Temperature	121 °C	250 °F	curing temp.