RheTech Products M12P250-01 12% Mica Reinforced Polypropylene Copolymer, Black
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Mica Filler |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products M12P250-01 12% Mica Reinforced Polypropylene Copolymer, Black.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Filler panelsHVAC ductsFan shroudsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.990 g/cc | 0.990 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 12 % | 12 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0114 cm/cm | 0.0114 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 69 | 69 | ASTM D2240 |
| Tensile Strength at Break | 23.4 MPa | 3400 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 1.52 GPa | 220 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm @Temperature 23.0 °C |
1.80 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 4.07 J | 3.00 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 74.4 °C | 166 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.2 °C | 135 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 193 - 221 °C | 380 - 430 °F | |
| Middle Barrel Temperature | 199 - 227 °C | 390 - 440 °F | |
| Front Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Nozzle Temperature | 210 - 221 °C | 410 - 430 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufFlex™ GTPE-2272SG-K8 TPE Compound
- Inno-Comp INNOPOL® CS 1-1120 AN 20% Talc-Filled Polypropylene Homopolymer
- Star Plastics PCGF20 Molding Grade PC with 20% Glass
- Saint-Gobain Meldin® 7001 CM Compression Molded Polyimide
- Zig Sheng Industrial ZISAMIDE® HP2201 Nylon 6
- Aclo Accutech ABS ABS831G30L Glass Reinforced
- Braskem TI4015F Impact Copolymer Polypropylene
- 3M 99786 Double Coated Tapes with 3M™ Adhesive 300MP
- Arlon P29514R020 0.0205" (0.521 mm) Semi-Cured Silicone Rubber with Fiberglass Substrate
- LATI LARPEEK 50 G/50 50% Glass Reinforced Polyetheretherketone (PEEK) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved