Ravago Manufacturing Americas Hylon® N1013STHL Nylon 6/6 (DAM)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylon® N1013STHL Nylon 6/6 (DAM).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 |
| Water Absorption | 0.70 % | 0.70 % | 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | 0.125 in; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 80 | 80 | ASTM D785 |
| Tensile Strength at Break | 89.6 MPa | 13000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 138 MPa | 20000 psi | ASTM D790 |
| Flexural Modulus | 3.79 GPa | 550 ksi | ASTM D790 |
| Izod Impact, Notched | 1.71 J/cm | 3.20 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | 0.0590 in, BK |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 282 - 299 °C | 540 - 570 °F | |
| Mold Temperature | 65.6 - 98.9 °C | 150 - 210 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | 0.18 % | 0.18 % | |
| Back Pressure | 0.138 - 0.414 MPa | 20.0 - 60.0 psi | |
| Screw Speed | 40 - 120 rpm | 40 - 120 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure | 750 to 1400 psi | |
| Injection Rate | Fast |
Users viewing this material also viewed the following:
- RheTech Products T20P252-00 20% Talc Reinforced Polypropylene, Natural
- Nabaltec NABALOX® NO 713-10 MF Reactive Alumina
- Indium Corp. Indalloy 215 Silver Solder Alloy
- Lord Adhesives Thermosetâ„¢ UR-329 Two Component Urethane Potting Compound
- SABIC Innovative Plastics LNP LUBRICOMP DL003EXJ PC
- Taiwan PU Corporation TPU-EH90 High Hydrolysis Resistance, Extrusion Molding Polyether Base TPU
- Shandong Dongyue Polymer HFC-125 Pentafluoroethane Refrigerant, CHF2CF3
- Dow Corning FOX® PMCP25 Flowable Oxide
- EDRO EDRO400™ #40 Prehardened Insert Quality Martensitic Stainless Steel
- Beijing Ranger Chem E-44 Semi Solid Epoxy Resin
Copyright © lookpolymers.com All Rights Reserved