Chase Plastics CP Pryme® NN200L (COND, 50% RH) Nylon 66, Internally Lubricated
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Chase Plastics |
| Trade Name | CP Pryme® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chase Plastics CP Pryme® NN200L (COND, 50% RH) Nylon 66, Internally Lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chase Plastics.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.7 MPa | 8800 psi | ASTM D638 |
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 |
| Flexural Modulus | 1.10 GPa | 160 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs Y200 YBr3·9H2O Yttrium bromide hydrate
- 3M Dyneon™ Fluorel™ FT-2320 Fluoroelastomer VF2 + HFP + TFE Terpolymer (discontinued **)
- Haynes Ultimet® alloy, aged 1000 hours at 649°C (1200°F)
- Materion Brush 1915â„¢ Heat Treated Temper Rod, 0.375" - 0.500"
- SABIC Innovative Plastics LNP LUBRILOY D20009 PC
- SABIC Innovative Plastics ULTEM HU2100 PEI
- Techmer ES HiFill® PEEK CF20 TL15 HF 20% Carbon Filled
- BorsodChem ONGROVIL S-465 Suspension PVC-Resin
- Plaslok 7021 Black Impact Grade Phenolic Molding Compound (discontinued **)
Copyright © lookpolymers.com All Rights Reserved