- Ravago Manufacturing Americas Hylon® N1000TL Nylon 6/6 (DAM) (discontinued **)
Ravago Manufacturing Americas Hylon® N1000TL Nylon 6/6 (DAM) (discontinued **)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylon® N1000TL Nylon 6/6 (DAM)
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Entec.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.018 cm/cm | 0.018 in/in | 0.125 in; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | ASTM D785 |
| Tensile Strength at Break | 65.5 MPa | 9500 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.21 GPa | 320 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 113 µm/m-°C @Temperature 20.0 °C |
63.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 229 °C | 445 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C | 160 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | 0.0590 in, BK |
| HB | HB | 0.118 in, BK |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.5 @Frequency 100 Hz |
3.5 @Frequency 100 Hz |
ASTM D150 |
| Dielectric Strength | 21.3 kV/mm | 540 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 277 - 293 °C | 530 - 560 °F | |
| Mold Temperature | 48.9 - 93.3 °C | 120 - 200 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | 0.18 % | 0.18 % | |
| Back Pressure | 0.138 - 0.414 MPa | 20.0 - 60.0 psi | |
| Screw Speed | 40 - 120 rpm | 40 - 120 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure | 400 to 1400 psi | |
| Injection Rate | Fast |
Users viewing this material also viewed the following:
- NOVA Chemicals Novapol® TR-0735-UG Hexene MDPE Rotational Molding Resin
- SolVin 561SF Vinyl Chloride - Vinyl Acetate copolymer Paste - filler
- Stir SpA C 2065 AT (PVC)
- UBE UBEPOL BR13HB HIPS (n-DM =0.03 wt %)
- Zhejiang Juner PC-A2-10 Top-Grade Flame Retardant UV-Resistant
- A. Schulman FORMION™ FI 241E Non-Reinforced, Extrusion Grade Ionomer Alloy
- ConocoPhillips ANDEROL® 6460 Synthetic Food Grade Gear Fluid
- AK Steel TRAN-COR® H-1 CARLITE® Grain Oriented Electrical Steel
- BASF Lupranate® 234 Isocyanate
- 3M Cushion-Mount™ 1720M Plus Plate Mounting Tape
Copyright © lookpolymers.com All Rights Reserved