Ravago Manufacturing Americas Hylon® N1000HL Nylon 6/6

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized
Manufacturer	Ravago Manufacturing Americas, LLC
Trade Name	Hylon®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ravago Manufacturing Americas Hylon® N1000HL Nylon 6/6.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Available in North America Additive: Heat Stabilizer and LubricantFeatures: Heat Stabilized and Lubricated RoHS Compliant Auto Specifications: FORD WSK-M4D648-A Color: Black Form: Pellets Processing Method: Injection Molding Properties are for dry polymer unless noted.Information provided by Ravago.

Physical Properties	Metric	English	Comments
Specific Gravity	1.14 g/cc	1.14 g/cc	ASTM D792
Water Absorption	1.3 % @Time 86400 sec	1.3 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.014 - 0.019 cm/cm @Thickness 3.17 mm	0.014 - 0.019 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	60	60	Conditioned; ASTM D785
	85	85	ASTM D785
Tensile Strength at Break	65.5 MPa	9500 psi	Conditioned; D638
	82.7 MPa	12000 psi	D638
Elongation at Break	30 %	30 %	ASTM D638
	200 %	200 %	Conditioned; ASTM D638
Flexural Strength	40.7 MPa	5900 psi	Conditioned; ASTM D790
	114 MPa	16500 psi	ASTM D790
Flexural Modulus	1.31 GPa	190 ksi	Conditioned; ASTM D790
	3.03 GPa	440 ksi	ASTM D790
Izod Impact, Notched	0.534 J/cm	1.00 ft-lb/in	ASTM D256
	1.33 J/cm	2.50 ft-lb/in	Conditioned; ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	82.8 µm/m-°C	46.0 µin/in-°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	221 °C	430 °F	Unannealed, Conditioned; ASTM D648
	238 °C	460 °F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	71.1 °C	160 °F	Unannealed, Conditioned; ASTM D648
	87.8 °C	190 °F	Unannealed; ASTM D648
Flammability, UL94	V-2 @Thickness 1.50 mm	V-2 @Thickness 0.0591 in	Conditioned
	V-2 @Thickness 1.50 mm	V-2 @Thickness 0.0591 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	Conditioned; ASTM D257
	1.00e+15 ohm-cm	1.00e+15 ohm-cm	ASTM D257
Dielectric Constant	3.7 @Frequency 100 Hz	3.7 @Frequency 100 Hz	ASTM D150
	6.0 @Frequency 100 Hz	6.0 @Frequency 100 Hz	Conditioned; ASTM D150
Dielectric Strength	21.7 kV/mm	550 kV/in	Conditioned; ASTM D149
	22.8 kV/mm	580 kV/in	Method A (Short-time); ASTM D149

Processing Properties	Metric	English	Comments
Melt Temperature	271 - 293 °C	520 - 560 °F
Mold Temperature	48.9 - 93.3 °C	120 - 200 °F
Drying Temperature	73.9 °C @Time 7200 - 14400 sec	165 °F @Time 2.00 - 4.00 hour
Moisture Content	<= 0.20 %	<= 0.20 %	Suggested Maximum
Back Pressure	0.345 - 0.689 MPa	50.0 - 100 psi
Screw Speed	40 - 140 rpm	40 - 140 rpm