A. Schulman FORMION™ FI 397 Ionomer
| Category | Polymer , Thermoplastic , Ionomer |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman FORMION™ FI 397 Ionomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.02 g/cc | 1.02 g/cc | ISO 1183/1 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm, Time 259000 sec |
0.0020 - 0.0060 in/in @Thickness 0.126 in, Time 72.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 63 | 63 | 15 sec delay; ISO 868 |
| Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | at max load; ISO 527 |
| Elongation at Break | 95 % | 95 % | ISO 527 |
| Flexural Modulus | 1.75 GPa | 254 ksi | Tangent; ISO 178 |
| Izod Impact, Notched (ISO) | 42.0 kJ/m² | 20.0 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 82.0 °C @Thickness 3.17 mm |
180 °F @Thickness 0.125 in |
ISO 75 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® N8855 TPE, Nylon Overmold
- Multibase Multi-Pro® 2510 XG Polypropylene
- Resin Technology Group TIGA 920H Flexible Silver Conductive
- Gharda Chemicals Gafone S 1320GF Polysulfone (PS) (discontinued **)
- Albis Plastics Cellulose Acetate CA700 , Unreinforced, 31% Plasticizer (discontinued **)
- ChevronTexaco LS Diesel 2
- Diamond Polymers Softflex® 2701-1502R
- Aclo Accutech Polypropylene Copolymer CP0437M20L Mica Reinforced
- Eurotec® Tecomid® NB40 MF20 GR003 FY70 PA6, 20% mineral filled, flame retardant - halogen free (RoHS compliant), grey RAL 7035
Copyright © lookpolymers.com All Rights Reserved