- Ravago Manufacturing Americas Hybrid B2026IU Polycarbonate + PBT Alloy
Ravago Manufacturing Americas Hybrid B2026IU Polycarbonate + PBT Alloy
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hybrid |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hybrid B2026IU Polycarbonate + PBT Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Available in North America UV Stabilizer Good Impact Resistance RoHS Compliant Form: Pellets Processing Method: Injection Molding Information provided by Ravago
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0090 cm/cm | 0.0060 - 0.0090 in/in | ASTM D955 |
| Melt Flow | 26 g/10 min @Load 5.00 kg, Temperature 260 °C |
26 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 54.5 MPa | 7900 psi | ASTM D638 |
| 55.0 MPa | 7980 psi | ISO 527-2 | |
| Tensile Modulus | 2.03 GPa | 295 ksi | ASTM D638 |
| 2.10 GPa | 305 ksi | ISO 527-2 | |
| Flexural Strength | 75.2 MPa | 10900 psi | ISO 178 |
| Flexural Yield Strength | 73.8 MPa | 10700 psi | ASTM D790 |
| Flexural Modulus | 2.24 GPa | 325 ksi | ASTM D790 |
| 2.35 GPa | 341 ksi | ISO 178 | |
| Izod Impact, Notched | 4.27 J/cm @Temperature -40.0 °C |
8.00 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| 7.47 J/cm @Temperature 22.8 °C |
14.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 35.7 kJ/m² @Temperature -40.0 °C |
17.0 ft-lb/in² @Temperature -40.0 °F |
ISO 180 |
| 60.9 kJ/m² @Temperature 22.8 °C |
29.0 ft-lb/in² @Temperature 73.0 °F |
ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | Unannealed; ASTM D648 |
| 103 °C | 217 °F | Unannealed; ISO 75-2/A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 238 - 266 °C | 460 - 510 °F | |
| Middle Barrel Temperature | 243 - 271 °C | 470 - 520 °F | |
| Front Barrel Temperature | 249 - 277 °C | 480 - 530 °F | |
| Nozzle Temperature | 254 - 271 °C | 490 - 520 °F | |
| Melt Temperature | 254 - 271 °C | 490 - 520 °F | |
| Mold Temperature | 54.4 - 82.2 °C | 130 - 180 °F | |
| Drying Temperature | 110 °C @Time 14400 - 18000 sec |
230 °F @Time 4.00 - 5.00 hour |
|
| Dry Time | <= 12.0 hour | <= 12.0 hour | |
| Moisture Content | <= 0.020 % | <= 0.020 % | Suggested Maximum |
| Shot Size | 50 - 80 % | 50 - 80 % | |
| Screw Speed | 50 - 80 rpm | 50 - 80 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Rate | Moderate | |
| Melt-Volume Flow Rate, 260°C/5.0 kg (in3/10 min) | 1.34 | ISO 1133 |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH T15040CR Polypropylene Homopolymer, Mineral Reinforced
- DuPont™ Sclairfilm® GL-3 LLDPE Film, Laminating, 38.1 µm Thickness (discontinued **)
- Kraton® G1654 E (SEBS) Linear Triblock Copolymer
- Gwent Electronic Materials C61003P7 Silver / Silver Chloride Paste
- Polyplastics FR-PET® BN9015 Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Flame retardant, General purpose
- A. Schulman POLYBATCH™ Orange 1096 Concentrate Based In Polyethylene
- Cossa Polimeri ESTAPROP 1050 V0 HF K Flame Retardant Polypropylene
- DuPont Performance Polymers Neoprene GRT M2 Polychloroprene Rubber
- Asahi Kasei Thermylene® P7-30FG-1804 30% Glass Fiber Reinforced, Chemically Coupled
Copyright © lookpolymers.com All Rights Reserved