SABIC Innovative Plastics LNP THERMOCOMP DX10313 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DX10313 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DX10313 is high modulus polycarbonate, 50% glass filled, with balanced flow and impact strength
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.61 g/cc | 1.61 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0015 cm/cm @Thickness 3.20 mm |
0.00050 - 0.0015 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound | 18 g/10 min @Load 5.00 kg, Temperature 300 °C |
18 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 152 MPa | 22000 psi | 5 mm/min; ISO 527 |
| 154 MPa | 22300 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.2 % | 2.2 % | 5 mm/min; ISO 527 |
| 2.3 % | 2.3 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 14.1 GPa | 2050 ksi | 1 mm/min; ISO 527 |
| 14.31 GPa | 2075 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 206 MPa | 29900 psi | 2 mm/min; ISO 178 |
| 222 MPa | 32200 psi | ASTM D790 | |
| Flexural Yield Strength | 207 MPa | 30000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 11.9 GPa | 1730 ksi | 2 mm/min; ISO 178 |
| 12.2 GPa | 1770 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.66 J/cm | 3.11 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.69 J/cm | 12.5 ft-lb/in | ASTM D4812 |
| Charpy Impact Unnotched | 4.30 J/cm² | 20.5 ft-lb/in² | ISO 179/2C |
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 179/2C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 16.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
8.89 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 128 °C @Thickness 3.20 mm |
262 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® INP630 ABS
- Polymer Resources PC-HM-FR1-[color]-3 Polycarbonate, 10% Glass Reinforced, Flame Retardant, UV-stabilized
- Solvay MIRANOL® HMD Surfactant
- Teknor Apex Monprene® MP-1766 Thermoplastic Elastomer
- SABIC Innovative Plastics NORYL FXN4020H PPE+HIPS
- A. Schulman POLYTROPE™ TPP 518 Injection Grade Olefinic Thermoplastic Elastomer
- Eastman Tenite 360E3V45512 Propionate Water Clear, Trsp
- 3M Scotchkote™ 165CS Urethane Sealer
- Dow Pellethane® 2354-65D Polyurethane Elastomer, Polyester Polycaprolactone Based (discontinued **)
Copyright © lookpolymers.com All Rights Reserved