Premix Thermoplastics PRE-ELEC® PP 1392 Carbon Black Filled Conductive Thermoplastic Compound

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with Carbon Black Filler
Manufacturer Premix Thermoplastics Inc.
Trade Name PRE-ELEC®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Thermoplastics PRE-ELEC® PP 1392 Carbon Black Filled Conductive Thermoplastic Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PRE-ELEC® PP 1392 is a carbon black filled conductive thermoplastic compound based on polypropylene. In addition to a low electrical resistivity PRE-ELEC® PP 1392 has an excellent balance of mechanical properties and is easy to injection mould. Applications: Injection moulded ESD products such as crates, boxes and tote bins for electronic components.Processing: PRE-ELEC® PP 1392 compound can be processed in the injection moulding machines using normal processing conditions as with polypropylene.Test Specimen: 10[mm] wide moulded rodInformation from Premix OY
Physical Properties Metric English Comments
Density 0.980 g/cc
0.0354 lb/in³
Thickness 102 microns
4.00 mil
Linear Mold Shrinkage 0.012 - 0.014 cm/cm
0.012 - 0.014 in/in
ISO 294-4
Melt Flow 7.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
7.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
35 g/10 min

@Load 5.00 kg,
Temperature 230 °C
35 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore A 97
97
ISO 868
Hardness, Shore D 72
72
ISO 868
Tensile Strength 27.0 MPa
3920 psi
ISO 527
Tensile Strength, Yield 27.0 MPa
3920 psi
ISO 527
Elongation at Break 8.0 %
8.0 %
ISO 527
Elongation at Yield 7.0 %
7.0 %
ISO 527
Flexural Modulus 1.50 GPa
218 ksi
ISO 178
Izod Impact, Notched (ISO) 15.0 kJ/m²

@Thickness 4.00 mm,
Temperature -20.0 °C
7.14 ft-lb/in²

@Thickness 0.157 in,
Temperature -4.00 °F
ISO 180
32.0 kJ/m²

@Thickness 4.00 mm,
Temperature 23.0 °C
15.2 ft-lb/in²

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Izod Impact, Unnotched (ISO) NB

@Thickness 4.00 mm,
Temperature 23.0 °C
NB

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
NB

@Thickness 4.00 mm,
Temperature -20.0 °C
NB

@Thickness 0.157 in,
Temperature -4.00 °F
ISO 180
Charpy Impact Unnotched NB

@Thickness 102 mm,
Temperature 23.0 °C
NB

@Thickness 4.00 in,
Temperature 73.4 °F
ISO 179
NB

@Thickness 102 mm,
Temperature -20.0 °C
NB

@Thickness 4.00 in,
Temperature -4.00 °F
ISO 179
Charpy Impact, Notched 1.40 J/cm²

@Thickness 102 mm,
Temperature -20.0 °C
6.66 ft-lb/in²

@Thickness 4.00 in,
Temperature -4.00 °F
ISO 179
1.50 J/cm²

@Thickness 102 mm,
Temperature 23.0 °C
7.14 ft-lb/in²

@Thickness 4.00 in,
Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 92.0 °C
198 °F
75/Method Bf
Deflection Temperature at 1.8 MPa (264 psi) 56.0 °C
133 °F
75/Method Af
Vicat Softening Point 88.0 °C
190 °F
ISO 306/B50
155 °C
311 °F
ISO 306/A50
Electrical Properties Metric English Comments
Volume Resistivity <= 1000 ohm-cm
<= 1000 ohm-cm
ISO D-257
Surface Resistance <= 10000 ohm
<= 10000 ohm
ISO IEC 61340-5-1
Processing Properties Metric English Comments
Melt Temperature 200 - 250 °C
392 - 482 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 60.0 - 80.0 °C
140 - 176 °F
Pre-drying
Dry Time 2 - 4 hour
2 - 4 hour
Injection Pressure 60.0 - 80.0 MPa
8700 - 11600 psi
Shelf Life 12.0 Month
12.0 Month
Normal Storing Conditions
Descriptive Properties Value Comments
Injection Speed Moderate