- Polymer Property : Flexural Modulus = 218 ksi
Polymer Property : Flexural Modulus = 218 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Modulus | 1.50 GPa | 218 ksi | |
| Plastcom SLOVALEN PC 59 GB 10 PP, 10% glass beads FeaturesCompouded homopolymer PP, with the content of 10% chemically bound glass beads and modifier of mechanical properties. Increased strength in comparison with unfilled PP. Use in all industry s.. |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | |
| Plastcom SLOVALEN PC 78 FRT 5 PP, glass fibre, mod. of mech. properties FeaturesModified copolymer PP for injection moulding, contains the modifier of mechanical properties and non halogen and free phosphor flame retardant. Increased strength in comparison with unfilled.. |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | ISO 178 |
| Premix Thermoplastics PRE-ELEC® PA 1412 Conductive Thermoplastic Compound PRE-ELEC® PA 1412 is a conductive thermoplastic compound based on polyamide 6. Conductivity is achieved by using conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® PA 1.. |
|||
| Flexural Modulus | 1.50 - 2.50 GPa | 218 - 363 ksi | ASTM D790-04 |
| Proto3000 Objet Digital Materials™ DM_8505Gray35 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr.. |
|||
| Flexural Modulus | 1.50 GPa @Temperature 90.0 °C |
218 ksi @Temperature 194 °F |
ISO 178, ASTM D790 |
| Nilit Nilamon A3 H K8 40% Mineral Reinforced PA66 Description: Nilamon A3 H K8 combines good stiffness with low warpage. It is used for applications which need a degree of rigidity, particularly at higher temperatures, but which need to stay flat a.. |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | ASTM D790 |
| Shell Carilon® D26VM100 Polyketone, High-Flow Injection Molding Grade
(discontinued **) Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer D26VM100 is a high-flow injection molding grade with mechanical properties which classify it as an .. |
|||
| Flexural Modulus | 1.50 GPa @Temperature 23.0 °C |
218 ksi @Temperature 73.4 °F |
ISO 178 |
| Polykemi AB POLYfill PPC K6020 S Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | ISO 178 |
| Total Finathene® SR 572 HDPE blow molding
(discontinued **) FINATHENE® SR 572 is a high density polyethylene produced by the slurry loop low pressure polymerization process. FINATHENE® SR 572 has been developed for the manufacturing of blow molded bottles .. |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | ISO 178 |
| Iran Petrochemical (PCC) EP-N31MA Polypropylene EP-N31MA is a high ultra fluidity heterophasic copolymer for thin walled injection molding the products offers a good stiffness impact balance. Applications: packaging, house ware and garden furnitu.. |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | ASTM D790 |
| Iran Petrochemical (PCC) Moplen Z 30 G Polypropylene Moplen Z 30 G is a high flow homopolymer for injection molding and compounding applications. Moplen Z 30 G exhibits a high stiffness and an outstanding processability for shorter cycle times and eas.. |
|||
| Flexural Modulus | 1.50 - 1.70 GPa | 218 - 247 ksi | ASTM D790 |
| Loxim 820 02C HB Polypropylene Compound, 20% Calcite Filled, Flame Retardant Information provided by Loxim Industries |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | 1% secant at 0.05 in/min; ASTM D790A |
| LyondellBasell Astryn BA905-74 Polypropylene Copolymer, Flame Retardant Key Features: medium high melt flow, medium high modulus, flame retardant, low specific gravity, good impact strengthApplications: battery jars, electrical componentsDescription: Astryn BA905-74 med.. |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP Thermocomp MX05038 PP (Europe-Africa-Middle East) Polypropylene compound, containing miniral. Added features include High ImpactThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics XYLEX FXY330DF PC+POLYESTER Polyester+PC alloy. Diffusion Effect. Color package may affect performance. |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | ASTM D790 |
| Styrolution Styrolux® GH 58 SBC Description: Styrolux® GH 58 is a high flow thermoplastic styrene-butadiene block copolymer with excellent mold release properties. It has crystal clarity, good toughness, good stiffness and warp.. |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | ISO 178 |
| Borealis HD822CF Polypropylene HD822CF is a polypropylene homopolymer. This grade is suitable for the manufacturing of unoriented films on cast and tubular quench film lines. Applications: food packaging, lamination films, statio.. |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | ISO 178 |
| Total PPC 10642 Polypropylene, Heterophasic Copolymer, Injection Molding Polypropylene PPC 10642 is a nucleated antistatic heterophasic copolymer with high Melt Flow index of 44 g/10 min.Polypropylene PPC 10642 is characterized by high fluidity with good mechanical prope.. |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | ISO 527-2 |
| Total PPH 7059 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 7059 is homopolymer.ApplicationATOFINA Polypropylene PPH 7059 is intended for extrusion of staple fibers for non-woven applications. It exhibits excellent spinning propert.. |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | At 2 mm/min; ISO 178 |
| Borealis Daplen™ EE109AE TPO Compound Daplen EE109AE is a 20% mineral and elastomer modified polypropylene compound intended for injection molding. Daplen EE109AE is a material with excellent impact /stiffness ratio. Thanks to its low .. |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | ISO 178 |
| Unitika EX-1030 PA6, Dry High-impact nylonInformation provided by Unitika Ltd. |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | ASTM-D790 |
| Polyram RamOfin PPC501 Polypropylene, Flame Retardant Flame retardant polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | 2 mm/min; ISO 178 |
| Eurostar Starflam MX06101 PP, Flame Retardant, Injection Molding Starflam MX06101 is an Unfilled, Halogen Free Flame Retardant Polypropylene Injection Molding ResinInformation provided by Eurostar. |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | ASTM D790 |
| Carmel Olefins CAPILENE® M 45 F Polypropylene Homopolymer CAPILENE® M 45 F is a polypropylene homopolymer developed for the production of cast films. It is formulated with slip and anti-blocking agents. They show high gloss, high transparency and good sti.. |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | XY; ASTM D790 |
| ALM PA 606-FR Filled Nylon 12 Prototyping Polymer Only commercially available fire retardant nylon 12 material, which meets FAR 25.853 60 second burn specification.The parts produced from PA 606-FR have a much smoother surface finish and sharper fe.. |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | XY direction; ASTM D790 |
| ALM PA 650 Nylon 12 SLS Prototyping Polymer Combines strength, durability (high impact) and chemical resistance and produces strong, durable, end use prototype parts. SL parts are less porous, more precise and have less noticeable build lines.. |
|||
| Flexural Modulus | 1.50 - 4.00 GPa @Temperature 60.0 - 90.0 °C |
218 - 580 ksi @Temperature 140 - 194 °F |
Average value: 2.84 GPa Grade Count:2 |
| Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Molded". Each property range of values reported is minimum and ma.. |
|||
| Flexural Modulus | 1.50 - 7.85 GPa | 218 - 1140 ksi | Average value: 4.04 GPa Grade Count:36 |
| Overview of materials for Polypropylene, Glass Reinforced, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Glass Reinforced, Impact Modified". Each property range of values reported is minimum and.. |
|||
| Flexural Modulus | 1.50 - 10.3 GPa | 218 - 1490 ksi | Average value: 5.11 GPa Grade Count:252 |
| Overview of materials for Nylon 6, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Glass Fiber Filled".Specific grades with glass content between 15% and 24% are included. Ea.. |
|||
| Flexural Modulus | 1.50 GPa | 218 ksi | ISO 178 |
| Unitika BV2120 PA66, Flame Retardant, Conditioned Information provided by Unitika Ltd. |
|||