Polyram PlusTek PA103 Nylon 6.6, Injection Molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA103 Nylon 6.6, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | DIN 53479 |
| Water Absorption | 8.5 % | 8.5 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 2.8 % | 2.8 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.014 - 0.018 cm/cm | 0.014 - 0.018 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM-D785 |
| Tensile Strength, Yield | 82.0 MPa | 11900 psi | ASTM-D638 |
| Elongation at Break | 50 % | 50 % | ASTM-D638 |
| Flexural Strength | 120 MPa | 17400 psi | ASTM D790 |
| Flexural Modulus | 2.70 GPa | 392 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.700 J/cm @Temperature 23.0 °C |
1.31 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous Use |
| 200 °C | 392 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | DIN 53461 |
| Flammability, UL94 | V-2 @Thickness 3.00 mm |
V-2 @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | DIN 53482 |
| Dielectric Constant | 3.6 @Frequency 1e+6 Hz |
3.6 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 120 kV/mm | 3050 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- G-11 Fiberglass Epoxy Laminate Sheet
- Mearthane Durethaneâ„¢ C 75A Polyurethane
- MTM Plastics Purpolen® PP Polypropylene Regrind
- Shanghai Ofluorine T-1 PVDF for coatings (DF-1)
- Samsung Cheil Industries Infino® NH-1035 PC, Unreinforced FR
- Teknor Apex Telcar® TL-1522G Thermoplastic Elastomer
- Cheng Yu Plastic T890G3 PBT, 30% Glass Fiber
- 3M 25M25X Protective UV Tape
- Solvay Specialty Polymers Solef® 20810 PVDF Copolymer (discontinued **)