- Teknor Apex Telcar® TL-1934C Thermoplastic Elastomer
Teknor Apex Telcar® TL-1934C Thermoplastic Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Teknor Apex Company |
| Trade Name | TELCAR® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex Telcar® TL-1934C Thermoplastic Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets Processing Method: Extrusion; Injection Molding Injection Notes: Injection Rate: Moderate-Fast Extrusion Notes: Screw Speed: 30 to 100 rpmInformation Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| Melt Flow | 25.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
25.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | 1 second; ASTM D2240 |
| Tensile Strength at Break | 8.41 MPa | 1220 psi | ASTM D412 |
| Elongation at Break | 680 % | 680 % | ASTM D412 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | V-0 | V-0 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 171 - 193 °C | 340 - 380 °F | |
| Middle Barrel Temperature | 177 - 199 °C | 350 - 390 °F | |
| Front Barrel Temperature | 182 - 204 °C | 360 - 400 °F | |
| Nozzle Temperature | 188 - 210 °C | 370 - 410 °F | |
| Zone 1 | 166 - 188 °C | 330 - 370 °F | |
| Zone 2 | 171 - 193 °C | 340 - 380 °F | |
| Zone 3 | 177 - 199 °C | 350 - 390 °F | |
| Zone 5 | 182 - 204 °C | 360 - 400 °F | |
| Die Temperature | 190 - 210 °C | 374 - 410 °F | |
| Melt Temperature | 188 - 210 °C | 370 - 410 °F | Processing Temperature |
| Mold Temperature | 25.0 - 65.6 °C | 77.0 - 150 °F | |
| Injection Pressure | 1.38 - 6.89 MPa | 200 - 1000 psi | |
| Back Pressure | 0.172 - 0.345 MPa | 25.0 - 50.0 psi | |
| Cushion | 0.381 - 2.54 cm | 0.150 - 1.00 in | |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Opaque |
Users viewing this material also viewed the following:
- Abatron 4838 A/B Filled Potting Compound (discontinued **)
- Lanxess Durethan® BKV 130 DUS008 901510 Nylon 6, Glass Fiber Reinforced, Impact Modified
- Multibase Multi-Flex® A 7101 TPE Thermoplastic Elastomer
- A. Schulman POLYFORT™ FPP 3717 Talc Filled Homopolymer Polypropylene (39.6% Mineral Content)
- Cresset Powers Cress-Alon™ A2350 2.35 r.v. Injection Molding Grade Nylon 6, 50% RH
- Cytec Thornel® T-650/35 6K Carbon Fiber, Polyacrylonitrile (PAN) Precursor
- BASF Palusol® 100 Silicate Panel
- Arlon 55100R030 0.030" (0.762 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Arlon 915-07R##-P1 0.015" (0.381 mm) Cured Self-fusing Silicone Tape
- Eurostar Star L PA66 15Y D52 PA66, Carbon Filled, Injection Molded
Copyright © lookpolymers.com All Rights Reserved