- Polymer Resources PC-GP2-TFE5 Polycarbonate, 5% PTFE, Wear Resistant, Medium Flow
Polymer Resources PC-GP2-TFE5 Polycarbonate, 5% PTFE, Wear Resistant, Medium Flow
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, PTFE Filled |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PC-GP2-TFE5 Polycarbonate, 5% PTFE, Wear Resistant, Medium Flow.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate, 5% PTFE, General Purpose, Medium Flow, Wear ResistantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 9.0 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C |
9.0 - 16 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 58.6 MPa | 8500 psi | ASTM D638 |
| Tensile Strength, Yield | 58.6 MPa | 8500 psi | ASTM D638 |
| Flexural Strength | 93.1 MPa | 13500 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm @Temperature 22.8 °C |
3.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Gardner Impact | 36.2 J | 26.7 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C | 278 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 131 °C | 267 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 288 - 310 °C | 550 - 590 °F | |
| Middle Barrel Temperature | 299 - 321 °C | 570 - 610 °F | |
| Front Barrel Temperature | 310 - 332 °C | 590 - 630 °F | |
| Melt Temperature | 316 - 343 °C | 600 - 650 °F | |
| Mold Temperature | 82.2 - 116 °C | 180 - 240 °F | |
| Drying Temperature | 118 - 124 °C | 245 - 255 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0005 |
Users viewing this material also viewed the following:
- Huntsman KRYSTALFLEX® PE 193 Polyurethane Optical Aliphatic Film
- KaMin Kamintex® D Kaolin Clay - Calcined, high solids
- SABIC Innovative Plastics LNP THERMOCOMP WH0200B PBT
- SABIC Innovative Plastics NORYL GTX GTX675 PPE+PA6
- Total PPM H250 Polypropylene, Homopolymer Medical Grade
- Borealis Daplen™ EF261AI Polypropylene TPO Compound
- ExxonMobil LLDPE LL 6301XR Molding Linear Low Density Polyethylene Resin (European Grade)
- DuPont Performance Polymers Zytel® 80G25HS BK117 Nylon 66 (Unverified Data**)
- 3M Scotch® 862 Reinforced Strapping Tape
- ATI Allegheny Ludlum Alloy 255 Stainless Steel, UNS S32550
Copyright © lookpolymers.com All Rights Reserved