Polymer Resources NY66-GP1-[color]-H General Purpose Nylon 66, Heat Stabilized

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized , Nylon 66, Unreinforced
Manufacturer	Polymer Resources, LTD
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polymer Resources NY66-GP1-[color]-H General Purpose Nylon 66, Heat Stabilized.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

General Purpose Nylon 66, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provided by Polymer Resources Corporation.

Physical Properties	Metric	English	Comments
Specific Gravity	1.14 g/cc	1.14 g/cc	ASTM D792
Linear Mold Shrinkage	0.012 - 0.018 cm/cm	0.012 - 0.018 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	82.7 MPa	12000 psi	ASTM D638
Tensile Strength, Yield	82.7 MPa	12000 psi	ASTM D638
Flexural Strength	117 MPa	17000 psi	ASTM D790
Flexural Modulus	3.10 GPa	450 ksi	ASTM D790
Izod Impact, Notched	0.534 J/cm @Temperature 22.8 °C	1.00 ft-lb/in @Temperature 73.0 °F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	229 °C	445 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	87.8 °C	190 °F	ASTM D648
UL RTI, Electrical	65.0 °C @Thickness 1.50 mm	149 °F @Thickness 0.0591 in	UL 746
	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in	UL 746
UL RTI, Mechanical with Impact	65.0 °C @Thickness 1.50 mm	149 °F @Thickness 0.0591 in	UL 746
	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in	UL 746
UL RTI, Mechanical without Impact	65.0 °C @Thickness 1.50 mm	149 °F @Thickness 0.0591 in	UL 746
	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in	UL 746
Flammability, UL94	V-2 @Thickness 1.50 mm	V-2 @Thickness 0.0591 in
	V-2 @Thickness 3.00 mm	V-2 @Thickness 0.118 in

Processing Properties	Metric	English
Rear Barrel Temperature	266 - 277 °C	510 - 530 °F
Middle Barrel Temperature	271 - 282 °C	520 - 540 °F
Front Barrel Temperature	277 - 288 °C	530 - 550 °F
Melt Temperature	277 - 293 °C	530 - 560 °F
Mold Temperature	65.6 - 93.3 °C	150 - 200 °F
Drying Temperature	73.9 - 85.0 °C	165 - 185 °F
Dry Time	3.00 - 4.00 hour	3.00 - 4.00 hour

Descriptive Properties	Value	Comments
Vent	0.0003