- Polykemi AB POLYfill PPH DNH15025 GF10 Polypropylene Homopolymer, Flame Retardant, Halogen Free, Glass Fibre-Reinforced
Polykemi AB POLYfill PPH DNH15025 GF10 Polypropylene Homopolymer, Flame Retardant, Halogen Free, Glass Fibre-Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Glass Fiber Filler , Polypropylene, Flame Retardant |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYfill PPH DNH15025 GF10 Polypropylene Homopolymer, Flame Retardant, Halogen Free, Glass Fibre-Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Filler Content | 10 % | 10 % | ±2%; Polykemi |
| Melt Index of Compound | 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 29.0 MPa | <= 4210 psi | ISO/R527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO/R527 |
| Flexural Strength | <= 50.0 MPa | <= 7250 psi | ISO 178 |
| Flexural Modulus | 3.10 GPa @Temperature 23.0 °C |
450 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -20.0 °C |
0.952 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 0.250 J/cm² @Temperature 23.0 °C |
1.19 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C | 279 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 112 °C @Load 5.001 kg |
234 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 156 °C @Load 1.00 kg |
313 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Glow Wire Test | 850 °C @Thickness 1.60 mm |
1560 °F @Thickness 0.0630 in |
IEC 695-2-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 220 °C | 356 - 428 °F | |
| Mold Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | in desiccant air dryer |
| 2 - 4 hour | 2 - 4 hour | in circulation dryer | |
| Injection Pressure | 40.0 - 110 MPa | 5800 - 16000 psi | |
| Back Pressure | 0.500 - 1.00 MPa | 72.5 - 145 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | 20-40 | % of injection pressure |
| Injection Speed () | Normal |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 51 HF UVT General Purpose Acrylic Resin
- Nylene® PA6/6 Glass Filled 5143 HS Nylon 6/6
- PTS Tristar® PC-10R-CL02(V38) 38 MFI Polycarbonate with Release
- Rostone Rosite® 4950BS SMC Thermoset Polyester, 10% Glass Reinforced (discontinued **)
- LATI Latamid SP2 H2 G/45 PA 6.12, 45% Glass Fiber Reinforced, Heat Stabilized
- Tisan TISOPLEN® 20% Talc Filled Heat Stabilized Copolymer Polypropylene
- Wall Colmonoy COLMONOY® 72 - Nickel-Based Alloy With Chromium Carbide
- Eagle Brass 770 Nickel Silver 18%, Spring
- DuPont Performance Polymers Hytrel® DYM250S BK472 TPC-ET+PBT (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved