Sumitomo Chemical Sumipex® LG Acrylic Resin, High Flow
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, High Flow, Molded |
| Manufacturer | Sumitomo Chemical |
| Trade Name | Sumipex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Chemical Sumipex® LG Acrylic Resin, High Flow.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product CharacteristicsHigh FlowInformation provided by Calsak Corporation
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 5.00 kg, Temperature 200 °C |
10 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 68.0 MPa | 9860 psi | ASTM D638 |
| Elongation at Yield | 10 % | 10 % | ASTM D638 |
| Tensile Modulus | 3.10 GPa | 450 ksi | ASTM D638 |
| Flexural Yield Strength | 115 MPa | 16700 psi | ASTM D790 |
| Izod Impact, Notched | 0.422 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
0.790 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C @Thickness 3.17 mm |
201 °F @Thickness 0.125 in |
annealed; ASTM D648 |
| Vicat Softening Point | 102 °C | 216 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.49 | 1.49 | ASTM D542 |
| Haze | 0.50 % | 0.50 % | ASTM D1003 |
| Transmission, Visible | 93 % | 93 % | Total light Transmission; ASTM D1003 |
Users viewing this material also viewed the following:
- Pinnacle Polymers 1512 Polypropylene Homopolymer, Fiber Spinning Grade
- Meilian Chemical PE900 BLACK MASTERBATCH
- Latrobe Lescalloy® HP 9-4-30 VAC-ARC ; 13.5 in RCS Billet Size High Strength Alloy Steel
- SABIC Innovative Plastics LNP LUBRICOMP RAL23 PA 66
- A. Schulman POLYFORT™ FPP 4020 20% Mineral-Filled Polypropylene
- Topas Advanced Polymers TOPAS® 8007S-04 Cyclic Olefin Copolymer (COC)
- Trelleborg Offshore Vikotherm™ 73785 Insulative Elastomer
- Chosun Refractories C18DX Magnesia Carbon Brick for Converter
- Arlon 51570R025 0.025" (0.635 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved