PolyOne Bergamid™ A700 TM-YF Polyamide 66 (Nylon 66)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Bergamid™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Bergamid™ A700 TM-YF Polyamide 66 (Nylon 66).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ±0.02 g/cm³; DIN 53479 |
| Water Absorption | 2.2 % | 2.2 % | 23C/50RH; ISO 62 |
| Water Absorption at Saturation | 6.7 % | 6.7 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa @Temperature 23.0 °C |
7250 psi @Temperature 73.4 °F |
dry as moulded; ISO 527-2/50 |
| Elongation at Yield | 6.0 % @Temperature 23.0 °C |
6.0 % @Temperature 73.4 °F |
dry as moulded; ISO 527-2/50 |
| Tensile Modulus | 2.00 GPa @Temperature 23.0 °C |
290 ksi @Temperature 73.4 °F |
dry as moulded; ISO 527-2/1 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 261 °C | 502 °F | ISO 3146 |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous (GTP 50% Tensile); IEC 60216 |
| 180 °C | 356 °F | Short Time; IEC 60216 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | Unannealed; ISO 75-2/B |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | Unannealed; ISO 75-2/A |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 90.0 kV/mm | 2290 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.016 @Frequency 1.00e+6 Hz |
0.016 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4.00 - 8.00 hour | 4.00 - 8.00 hour | Desiccant Dryer |
| Back Pressure | 50.0 - 150 MPa | 7250 - 21800 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Forms | Pellets | |
| Generic Material | Nylon 66 | |
| Generic Name | Polyamide 66 (Nylon 66) | |
| Processing Method | Extrusion | |
| Injection Molding | ||
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| RoHS Compliance | RoHS Compliant | |
| UL File Number | E76261 | Global |
Users viewing this material also viewed the following:
- Polimeri Europa Extir® Verdi VR A3000 AE Expandable Polystyrene - Flame Retardant
- Polimersan Plastics POLIPOLEN® (Polyethylene) HD-PE 500
- DSM Akulon® Ultraflow™ K-FHG7 Nylon 6-35% Glass Reinforced (European Grade) (Dry) (discontinued **)
- SABIC Innovative Plastics LNP THERMOCOMP WF0049 PBT (Europe-Africa-Middle East)
- DuPont Elvax® 3165 Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion, Blown Film
- DSM Novamid® 2420A PA666
- Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 25% Cold Reduction
- Asahi Kasei ASACLEAN PF Purging Compound
- Asahi Kasei Thermylene® P7-45FG-0790 45% Glass Fiber Reinforced, Heat Stabilized
Copyright © lookpolymers.com All Rights Reserved