PlastiComp Complet® LGF30 - PA66 Nylon 66, 30% Long Glass Fiber Reinforced

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer	PlastiComp
Trade Name	Complēt®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PlastiComp Complet® LGF30 - PA66 Nylon 66, 30% Long Glass Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Nylon 66 with 30% long glass fiber reinforcementInformation provided by PlastiComp, Inc.

Physical Properties	Metric	English	Comments
Specific Gravity	1.37 g/cc	1.37 g/cc	ASTM D-792
Filler Content	30 %	30 %	Long Glass Fiber

Mechanical Properties	Metric	English	Comments
Tensile Strength	183 MPa	26500 psi	ASTM D-638
Elongation at Break	2.0 - 3.0 %	2.0 - 3.0 %	ASTM D-638
Tensile Modulus	10.345 GPa	1500.4 ksi	ASTM D-638
Flexural Strength	283 MPa	41000 psi	ASTM D-790
Flexural Modulus	9.655 GPa	1400 ksi	ASTM D-790
Izod Impact, Notched	2.67 J/cm	5.00 ft-lb/in	ASTM D-256
Izod Impact, Unnotched	13.884 J/cm	26.010 ft-lb/in	ASTM D-4812

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	249 °C	480 °F	ASTM D-648

Processing Properties	Metric	English
Rear Barrel Temperature	282 - 299 °C	540 - 570 °F
Middle Barrel Temperature	288 - 304 °C	550 - 580 °F
Front Barrel Temperature	293 - 310 °C	560 - 590 °F
Nozzle Temperature	288 - 304 °C	550 - 580 °F
Melt Temperature	293 - 310 °C	560 - 590 °F
Mold Temperature	93.3 °C	200 °F
Injection Velocity	50.8 - 76.2 mm/sec	2.00 - 3.00 in/sec
Drying Temperature	85.0 °C @Time 14400 sec	185 °F @Time 4.00 hour
Moisture Content	<= 0.18 %	<= 0.18 %
Back Pressure	0.172 - 0.345 MPa	25.0 - 50.0 psi
Cushion	0.635 cm	0.250 in
Screw Speed	30 - 50 rpm	30 - 50 rpm

Descriptive Properties	Value	Comments
Injection Pressure	Medium to maximum