SABIC Innovative Plastics LNP Lubricomp ZFL36CCX PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp ZFL36CCX PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* ZFL36CCX is a compound based on PPE+PS Blend resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D 792 |
| 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.080 % | 0.080 % | 23°C / 50% RH; ISO 62 |
| 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0028 cm/cm @Time 86400 sec |
0.0028 in/in @Time 24.0 hour |
ISO 294 |
| 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.0028 cm/cm @Time 86400 sec |
0.0028 in/in @Time 24.0 hour |
ISO 294 |
| 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 109 MPa | 15800 psi | ASTM D 638 |
| 109 MPa | 15800 psi | ISO 527 | |
| Elongation at Break | 1.6 % | 1.6 % | ISO 527 |
| 1.7 % | 1.7 % | ASTM D 638 | |
| Tensile Modulus | 10.16 GPa | 1474 ksi | 1 mm/min; ISO 527 |
| 10.61 GPa | 1539 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 168 MPa | 24400 psi | ISO 178 |
| 172 MPa | 24900 psi | ASTM D 790 | |
| Flexural Modulus | 9.99 GPa | 1450 ksi | ASTM D 790 |
| 10.55 GPa | 1530 ksi | ISO 178 | |
| Izod Impact, Notched | 1.22 J/cm @Temperature 23.0 °C |
2.29 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 5.34 J/cm @Temperature 23.0 °C |
10.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 34.0 kJ/m² @Temperature 23.0 °C |
16.2 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Coefficient of Friction, Dynamic | 0.50 | 0.50 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.45 | 0.45 | ASTM D 3702 Modified |
| K (wear) Factor | 90.6 x 10-8 mm³/N-M | 45.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Rogers Corporation Bisco™ HT-1200 Solid Silicone Rubber
- PolyOne Elastamax™ EG-9172 Thermoplastic Elastomer (TPE)
- Dow INSPIRE™ TF2300 Thermoplastic Polyolefin (discontinued **)
- LG Chemical LUPOL TE5108H PP+Rubber+MF, High Impact
- Iran Petrochemical (PCC) EX7C HF4750K High Density Polyethylene
- Ensinger Tecapeek® XP-101 Compression Molded PEEK Compound, Filled with 15% Graphite and 10% PTFE
- Arkema Group Rilsan® Powder T GREY 5161 MAC Nylon 11, Coating Grade
- 3M FS0592 Clear Polystyrene Label Products
- NOVA Chemicals Sclair® 2715 HDPE Injection Molding Resin (discontinued **)
- Diamond Polymers ABS/PC 9801
Copyright © lookpolymers.com All Rights Reserved