Plastcom PLASTAMID® 6 GF 15 PA6 reinforced with glass fiber

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced
Manufacturer	Plastcom spol. s r.o.
Trade Name	PLASTAMID®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Plastcom PLASTAMID® 6 GF 15 PA6 reinforced with glass fiber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PA 6 for injection molding, reinforced with 15% glass fiber. Application: applied in automotive, electrical, engineering and consumer-goods industry, eg.: grips for electro tools, hobby tools, gears, cases of the electrotools, cooling screws of blowers, electromotors, carrying parts in the automotive industry. Delivered in black color.Information Provided by Plastcom spol. s r.o.

Physical Properties	Metric	English	Comments
Density	1.23 g/cc	0.0444 lb/in³	STN EN ISO 1183-1
Linear Mold Shrinkage	0.0070 cm/cm	0.0070 in/in	STN EN ISO 294-4
Linear Mold Shrinkage, Transverse	0.015 cm/cm	0.015 in/in	STN EN ISO 294-4
Melt Flow	3.0 g/10 min @Load 2.16 kg, Temperature 230 °C	3.0 g/10 min @Load 4.76 lb, Temperature 446 °F	STN EN ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	90.0 MPa	13100 psi	STN EN ISO 527-2
Elongation at Break	4.0 %	4.0 %	STN EN ISO 527-2
Tensile Modulus	5.50 GPa	798 ksi	STN EN ISO 527-2
Flexural Strength	150 MPa	21800 psi	STN EN ISO 178
Flexural Modulus	4.40 GPa	638 ksi	STN EN ISO 178
Charpy Impact Unnotched	2.00 J/cm² @Temperature 23.0 °C	9.52 ft-lb/in² @Temperature 73.4 °F	STN EN ISO 179
	2.00 J/cm² @Temperature -20.0 °C	9.52 ft-lb/in² @Temperature -4.00 °F	STN EN ISO 179
Charpy Impact, Notched	0.200 J/cm² @Temperature 23.0 °C	0.952 ft-lb/in² @Temperature 73.4 °F	STN EN ISO 179
	0.200 J/cm² @Temperature -20.0 °C	0.952 ft-lb/in² @Temperature -4.00 °F	STN EN ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	STN EN 11357-1
Deflection Temperature at 1.8 MPa (264 psi)	200 °C	392 °F	STN EN ISO 75-2 (A)
Vicat Softening Point	200 °C	392 °F	STN EN ISO 306
Flammability, UL94	HB	HB
Glow Wire Test	650 °C @Thickness 3.00 mm	1200 °F @Thickness 0.118 in	STN EN 60695-2-12

Processing Properties	Metric	English	Comments
Melt Temperature	250 - 270 °C	482 - 518 °F
Mold Temperature	70.0 - 80.0 °C	158 - 176 °F
Drying Temperature	80.0 °C @Time 14400 sec	176 °F @Time 4.00 hour
Moisture Content	0.15 %	0.15 %	STN EN ISO 3344
Injection Pressure	70.0 - 120 MPa	10200 - 17400 psi

Descriptive Properties	Value	Comments
Color	Black