Cosmic Plastics 3D36 Thermoset Polyester Molding Compound
| Category | Polymer , Thermoset , Polyester, TS , Polyester (Thermoset) - Rigid |
| Manufacturer | Cosmic Plastics |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cosmic Plastics 3D36 Thermoset Polyester Molding Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.00 g/cc | 0.0723 lb/in³ | |
| Water Absorption | 1.0 % | 1.0 % | 48 hrs, 50°C |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | typical. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 24.0 - 48.0 MPa | 3480 - 6960 psi | |
| Flexural Strength | 76.0 MPa | 11000 psi | |
| Compressive Strength | 138 MPa | 20000 psi | |
| Izod Impact, Notched | 3.20 J/cm | 5.99 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | Heat Distortion temperature |
| Flammability, UL94 | V-1 @Thickness 3.20 mm |
V-1 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 5.5 @Frequency 1e+6 Hz |
5.5 @Frequency 1e+6 Hz |
Wet |
| 6.0 @Frequency 1000 Hz |
6.0 @Frequency 1000 Hz |
Wet | |
| Dielectric Strength | 14.0 kV/mm | 356 kV/in | Wet, Step by Step |
| Dissipation Factor | 0.030 @Frequency 1e+6 Hz |
0.030 @Frequency 1e+6 Hz |
Wet |
| 0.050 @Frequency 1000 Hz |
0.050 @Frequency 1000 Hz |
Wet | |
| Arc Resistance | 150 sec | 150 sec |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 135 - 165 °C | 275 - 329 °F | Molding temperature |
Users viewing this material also viewed the following:
- NEXA® PFX8050 Perfluoroelastomer
- Reliance Industries Reclair M26500 Polyethylene
- Samsung Cheil Industries Infino® GP-5300G PBT, Glass Filled
- Westlake Plastics Radel® R 5500 Polyphenylsulfone For Medical Applications
- A. Schulman POLYBATCH™ XU-2013-LD Concentrate Based In LDPE
- DSM Akulon® K224-HG4 Nylon 6-20% Glass Reinforced (European Grade) (Cond)
- Arlon R37208T017 0.017" (0.432 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Liner
- Axiall 801-90B Moldings & Extrusions Flexible PVC
- Azoty Tarnow™ Tarnamid® T-27 MCS 850 Polyamide 6 - Flame Retarded, Unreinforced
- Aremco Ceramacast™ 575 Alumina Fine Grain Potting Compound
Copyright © lookpolymers.com All Rights Reserved