LATI Latene® 7H2W T-V0E PP Homopolymer, Mineral Reinforced, Heat Stabilized, Flame Retardant

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant , Polypropylene, Mineral Reinforced
Manufacturer LATI
Trade Name Latene®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latene® 7H2W T-V0E PP Homopolymer, Mineral Reinforced, Heat Stabilized, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polypropylene homopolymer (PPh) based compound. Heat stabilized. Metal stabilized. Mineral filler. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
Linear Mold Shrinkage, Flow 0.0075 - 0.0095 cm/cm
0.0075 - 0.0095 in/in
Linear Mold Shrinkage, Transverse 0.0070 - 0.0090 cm/cm
0.0070 - 0.0090 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 10.0 MPa

@Temperature 90.0 °C
 1450 psi

@Temperature 194 °F
15.0 MPa

@Temperature 60.0 °C
 2180 psi

@Temperature 140 °F
25.0 MPa

@Temperature 23.0 °C
 3630 psi

@Temperature 73.4 °F
Elongation at Break 3.7 %

@Temperature 23.0 °C
 3.7 %

@Temperature 73.4 °F
6.0 %

@Temperature 60.0 °C
 6.0 %

@Temperature 140 °F
10 %

@Temperature 90.0 °C
 10 %

@Temperature 194 °F
Elongation at Yield 2.3 %

@Temperature 23.0 °C
 2.3 %

@Temperature 73.4 °F
5.5 %

@Temperature 60.0 °C
 5.5 %

@Temperature 140 °F
6.5 %

@Temperature 90.0 °C
 6.5 %

@Temperature 194 °F
Tensile Modulus 1.00 GPa

@Temperature 90.0 °C
 145 ksi

@Temperature 194 °F
1.45 GPa

@Temperature 60.0 °C
 210 ksi

@Temperature 140 °F
3.50 GPa

@Temperature 23.0 °C
 508 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 0.650 J/cm²

@Temperature -20.0 °C
 3.09 ft-lb/in²

@Temperature -4.00 °F
2.00 J/cm²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.230 J/cm²

@Temperature -20.0 °C
 1.09 ft-lb/in²

@Temperature -4.00 °F
0.250 J/cm²

@Temperature 23.0 °C
 1.19 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 105 °C
221 °F
Deflection Temperature at 0.46 MPa (66 psi) 115 °C
239 °F
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
Vicat Softening Point 70.0 °C

@Load 5.00 kg
 158 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
5VB

@Thickness 3.00 mm
 5VB

@Thickness 0.118 in
Oxygen Index 27 %
27 %
Glow Wire Test 960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
A solution
Processing Properties Metric English Comments
Melt Temperature 180 - 220 °C
356 - 428 °F
Mold Temperature 20.0 - 40.0 °C
68.0 - 104 °F
Drying Temperature 80.0 - 90.0 °C

@Time 10800 sec
 176 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa