- Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
- PTS Trilac® FR1 ABS- Flame Retardant ABS Resin (Unverified Data**)
PTS Trilac® FR1 ABS- Flame Retardant ABS Resin (Unverified Data**)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Trilac® FR1 ABS- Flame Retardant ABS Resin
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | 24 Hr.; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
6.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 36.5 MPa @Thickness 3.17 mm |
5300 psi @Thickness 0.125 in |
ASTM D638 |
| Tensile Modulus | 2.17 GPa | 315 ksi | ASTM D638 |
| Flexural Strength | 64.1 MPa @Thickness 3.17 mm |
9300 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 2.24 GPa @Thickness 3.17 mm |
325 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 1.49 J/cm @Thickness 3.17 mm |
2.80 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 76.7 °C @Thickness 3.17 mm |
170 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 60.0 °C | 140 °F | |
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
|
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 177 °C | 350 °F | |
| Middle Barrel Temperature | 204 °C | 400 °F | |
| Front Barrel Temperature | 216 °C | 420 °F | |
| Melt Temperature | 232 - 249 °C | 450 - 480 °F | |
| Mold Temperature | 54.4 - 71.1 °C | 130 - 160 °F | |
| Drying Temperature | 87.8 - 93.3 °C | 190 - 200 °F | |
| Dry Time | 2 - 24 hour | 2 - 24 hour | |
| Injection Pressure | 55.2 - 82.7 MPa | 8000 - 12000 psi | |
| Back Pressure | 0.689 MPa | 100 psi | |
| Screw Speed | 50 - 60 rpm | 50 - 60 rpm |
Users viewing this material also viewed the following:
- ExxonMobil Vyram™ 9111-35W222 Thermoplastic Elastomer (discontinued **)
- MBA Polymers PS 3122 Post-consumer recycled impact modified polystyrene
- Styrolution Terblend® N NG-02 8% Glass Filled ABS/PA6 (Dry)
- Master Bond MB250NT Low viscosity ethyl cyanoacrylate
- Unipetrol PP MONSTEN® GB 005 Polypropylene Homopolymer
- CPT C-Flex® R70-051 Clear Biocompatible TPE
- Fainplast Compounds GS 70/BT Flexible PVC, Injection Molding for Footwear
- EMS-Grivory Grivory® L 25 W 40 HL X PA12-I
- 3D Systems Accura® 45HC Plastic for SLA® Systems
- Braskem H 604 Thermoforming & Extrusion Polypropylene Homopolymer
Copyright © lookpolymers.com All Rights Reserved