Covestro Bayblend® 2253 Polycarbonate + ABS Blend, Extrusion (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Covestro Bayblend® 2253 Polycarbonate + ABS Blend, Extrusion
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Properties tested in transverse direction (worst case) on 125-mil (3.2 mm) extruded sheets specimens with
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | ASTM D785 |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | ASTM D638 |
| Flexural Yield Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 2.10 J/cm @Temperature -40.0 °C |
3.93 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| 5.30 J/cm @Thickness 3.17 mm |
9.93 ft-lb/in @Thickness 0.125 in |
ASTM D256 | |
| Impact Test | 45.0 J @Thickness 3.20 mm |
33.2 ft-lb @Thickness 0.126 in |
Instrumented Impact, Total Energy; 3.2 mm thick, 7.6 mph, 1.5 in. clamp, 0.5 in. dart; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C @Thickness 3.17 mm |
210 °F @Thickness 0.125 in |
ASTM D648 |
| Vicat Softening Point | 110 °C | 230 °F | Rate B; ISO 306 |
| UL RTI, Electrical | 85.0 °C @Thickness 1.57 mm |
185 °F @Thickness 0.0618 in |
|
| UL RTI, Mechanical with Impact | 85.0 °C @Thickness 1.57 mm |
185 °F @Thickness 0.0618 in |
|
| UL RTI, Mechanical without Impact | 85.0 °C @Thickness 1.57 mm |
185 °F @Thickness 0.0618 in |
|
| Flammability, UL94 | HB @Thickness 1.57 mm |
HB @Thickness 0.0618 in |
|
| HB @Thickness 1.57 mm |
HB @Thickness 0.0618 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 175 V | 175 V | IEC 112 |
Users viewing this material also viewed the following:
- MV Labs ND810 Nd2O3 Neodymium oxide
- Momentive Performance Materials RTV6166 Clear Potting/Encapsulating Gel
- SABIC Innovative Plastics LNP STAT-LOY AF3029U ABS (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP Thermocomp MF0044E PP (Europe-Africa-Middle East)
- A. Schulman SCHULADUR® A GF10 10% Glass Fiber Reinforced PBT
- TSE Industries Millathane® 26 Millable Polyether Urethane for Food Contact Applications
- UBE Tyranno Grade LoxM Ceramic High Temperature Fiber
- 3M 5360K Silicone Rubber Termination Kits
- AK Steel 15-5 PH® Precipitation Hardening Stainless Steel, Condition H 1150
Copyright © lookpolymers.com All Rights Reserved