Nilit FRIANYL A63 SG40 Nylon 6.6 for injection molding, 40% mineral filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Mineral Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 SG40 Nylon 6.6 for injection molding, 40% mineral filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ISO 1183 |
| Water Absorption | 1.2 - 2.0 % | 1.2 - 2.0 % | ISO 62 |
| Water Absorption at Saturation | 5.0 - 7.0 % | 5.0 - 7.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0090 - 0.017 cm/cm | 0.0090 - 0.017 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 155 MPa | 22500 psi | ISO 2039-1 |
| Tensile Strength at Break | 76.0 MPa | 11000 psi | ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 |
| Tensile Modulus | 4.40 GPa | 638 ksi | ISO 527 |
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| Flexural Modulus | 3.90 GPa | 566 ksi | ISO 178 |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | DIN 53453 |
| 2.20 J/cm² @Temperature -40.0 °C |
10.5 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | DIN 53453 |
| 0.180 J/cm² @Temperature -40.0 °C |
0.857 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 100 °C | 212 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 303 PC (Asia Pacific)
- SABIC Innovative Plastics LNP Lubricomp ZFL24 PPO
- Techmer ES HiFill® PA6 GF20 L 20% Glass Filled
- Stir SpA SR 60 K8 (PVC)
- Chase Plastics CP Pryme® AC100-9 Acetal Copolymer Molding Resin
- A. Schulman POLYFORT™ PP 7001
- Barlog Plastics KEBAFLOW HF140 LCP, 40% glass fiber reinforced
- Beijing Chemical Industry KAIFA® 304-G20 PBT Resin
- BASF Elastollan® C-74D Polyester Type Polyurethane Elastomer
Copyright © lookpolymers.com All Rights Reserved