SABIC Innovative Plastics Cycoloy® C1200HF PC+ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® C1200HF PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC+ABS, excellent flow/impact/high heat resistance. Low temperature ductility. For automotive, appliance and electrical components.
Physical Properties Metric English Comments
Specific Gravity 1.15 g/cc
1.15 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 19 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 19 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ASTM D1238
Melt Index of Compound 24 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 24 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 55.0 MPa
7980 psi
50 mm/min; ISO 527
57.0 MPa
8270 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 114 %
114 %
50 mm/min; ISO 527
150 %
150 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 4.8 %
4.8 %
50 mm/min; ISO 527
5.0 %
5.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.27 GPa
329 ksi
50 mm/min; ASTM D638
2.36 GPa
342 ksi
1 mm/min; ISO 527
Flexural Strength 86.0 MPa
12500 psi
ISO 178
Flexural Yield Strength 88.0 MPa
12800 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.25 GPa
326 ksi
ISO 178
2.34 GPa
339 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 5.87 J/cm
11.0 ft-lb/in
ASTM D256
4.80 J/cm

@Temperature -30.0 °C
 8.99 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 49.0 kJ/m²
23.3 ft-lb/in²
80*10*4mm, Cut; ISO 180/1A
34.0 kJ/m²

@Temperature -30.0 °C
 16.2 ft-lb/in²

@Temperature -22.0 °F
 80*10*4mm, Cut; ISO 180/1A
Dart Drop, Total Energy 54.0 J

@Temperature 23.0 °C
 39.8 ft-lb

@Temperature 73.4 °F
 ASTM D3763
54.0 J

@Temperature -30.0 °C
 39.8 ft-lb

@Temperature -22.0 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 40.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 130 °C
266 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
129 °C

@Thickness 3.20 mm
 264 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
112 °C

@Thickness 3.20 mm
 234 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 130 °C
266 °F
Rate B/50; ISO 306
UL RTI, Electrical 105 °C
221 °F
UL 746B
UL RTI, Mechanical with Impact 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical without Impact 105 °C
221 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.19 mm
 HB

@Thickness 0.0469 in
 UL 94
Electrical Properties Metric English Comments
Comparative Tracking Index 250 - 400 V
250 - 400 V
UL 746A
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
UL 746A
High Amp Arc Ignition, HAI 60 - 120 arcs
60 - 120 arcs
UL 746A