Nilit FRIANYL B63 HS-GV40 Nylon 6 for injection molding, 40% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 HS-GV40 Nylon 6 for injection molding, 40% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Water Absorption | 1.4 - 1.9 % | 1.4 - 1.9 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 7.0 % | 6.0 - 7.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0060 - 0.014 cm/cm | 0.0060 - 0.014 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 120 MPa | 17400 psi | ISO 2039-1 |
| Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 9.50 GPa | 1380 ksi | ISO 527 |
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 |
| Flexural Modulus | 7.90 GPa | 1150 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | ISO 179/1eA |
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 115 °C | 239 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Multibase SILASTIC® C7-4535 DICUP R Dow-Corning Biomedical Grade ETR Elastomer
- Covestro Apec® 2000 Polycarbonate (discontinued **)
- LG Chemical LUMID GP3400A(W) PA6+MF40%, General Purpose
- SABIC Innovative Plastics ULTEM HU1100 PEI (Asia Pacific)
- Styrolution Terblend® N NG-02 8% Glass Filled ABS/PA6 (Dry)
- A. Schulman FORMION™ FI 335 Ionomer
- A. Schulman POLYFORT™ FPP 1200 Calcium Carbonate-Filled Homopolymer Polypropylene
- ConocoPhillips SynXPA® 150 R&O Oil
- Chengdu Polyster H3303 Thermoplastic Polyether-ester Elastomer (TPEE)
- Diamond Polymers Centrex® 825 Sheet Extrusion Grade
Copyright © lookpolymers.com All Rights Reserved