E-Polymers TEKAMID® TA210SG30 Impact Modified, 30% Glass Fiber Reinforced PA66, DAM
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Reinforced, Impact Grade |
| Manufacturer | E-Polymers Co. Ltd. |
| Trade Name | TEKAMID® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | E-Polymers TEKAMID® TA210SG30 Impact Modified, 30% Glass Fiber Reinforced PA66, DAM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass Fiber reinforced, Impact resistanceInformation provided by E-Polymers Co. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | 23°C/24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D786 |
| Tensile Strength, Yield | 130 MPa | 18900 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Yield Strength | 195 MPa | 28300 psi | ASTM D790 |
| Flexural Modulus | 6.80 GPa | 986 ksi | ASTM D790 |
| Izod Impact, Notched | 2.30 J/cm | 4.31 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ASTM D2133 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable WELB406L Polyvinyl Chloride, Flexible (PVC, Flexible)
- MV Labs NI410 NiCl2·6H2O Nickel chloride hexahydrate
- Polimersan Plastics POLITEF® (PTFE) with 25% Carbon
- Heatbath/Park Sta-Hard 45 High Speed Hardening Salt
- SGL Carbon Group SIGRAFIL C® C25 S001 EPY Staple Carbon Fiber, Epoxy Sizing
- Lubrizol ESTANE® 5702F2 Ester Based Thermoplastic Polyurethane (European Grade)
- Ecomass® 720ZD91 Tungsten Filled ABS
- Arlon R37230R006 0.006" (0.152 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Substrate
- 3M 520ETL Sandblast Stencil
- Asia International Enterprise (Hong Kong) 60G8-43GF Nylon 66, 43% Filled
Copyright © lookpolymers.com All Rights Reserved