- Nilit FRIANYL A63 KV20 Nylon 6.6 for injection molding, 20% glass ball reinforced
Nilit FRIANYL A63 KV20 Nylon 6.6 for injection molding, 20% glass ball reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 KV20 Nylon 6.6 for injection molding, 20% glass ball reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Water Absorption | 1.7 - 2.7 % | 1.7 - 2.7 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 8.0 % | 6.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.012 - 0.020 cm/cm | 0.012 - 0.020 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ISO 527 |
| Elongation at Break | 6.0 % | 6.0 % | ISO 527 |
| Tensile Modulus | 3.70 GPa | 537 ksi | ISO 527 |
| Flexural Strength | 100 MPa | 14500 psi | ISO 178 |
| Flexural Modulus | 3.20 GPa | 464 ksi | ISO 178 |
| Charpy Impact Unnotched | 2.40 J/cm² | 11.4 ft-lb/in² | DIN 53453 |
| 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179/1eU | |
| 2.00 J/cm² @Temperature -40.0 °C |
9.52 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | DIN 53453 |
| 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 100 °C | 212 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Resinlab® CYNERGY CA6310 Adhesive
- Plastcom SLOVALEN PC 53 N Polypropylene Copolymer, UV Stabilization
- DuPont Performance Polymers Zytel® 158L NC010 Nylon 612 (Unverified Data**)
- Karina E 32/76-FC-LMP Orange Color Concentrate for PVC
- Kolon KOPA® KN178MT40 M/F Reinforced Nylon 6
- Shin-Etsu Silicones X-33-156-20 Silicone Primer
- Shinkong Synthetic Fibers Shinite® T102G15 PET, 15% Glass Filled, Fire Retardant
- Zyvex Performance Materials Aroply™ 350 Nano-Engineered Composite Film Adhesive
- EMS-Griltech Griltex® 2A Copolyamide Hotmelt Adhesive (Technical Applications)
- 3M Scotch-Weld™ 2214 Regular Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved