A. Schulman ComAlloy Hiloy® 633 Nylon 6/6, Glass Reinforced, Flow Enhanced, UL
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Hiloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Hiloy® 633 Nylon 6/6, Glass Reinforced, Flow Enhanced, UL.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.33% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 166 MPa | 24100 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 228 MPa | 33100 psi | ASTM D790 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.30 J/cm | 11.8 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 255 - 275 °C | 491 - 527 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 271 - 285 °C | 520 - 545 °F |
Users viewing this material also viewed the following:
- Plenco 7466 Phenolic, Nodular, Injection Molded (discontinued **)
- Huntsman IROGRAN® A 85 P 4944 Ether-Based TPU-For Cable Industry
- LG Chemical Lupoy 1320C-07 Polycarbonate Resin
- H.C. Starck Amperit® 704.092 Chromium Oxide (Cr2O3) 99.5%
- Special Metals Electroformed Nickel, 13 Micron (0.5 mil) Foil, Electroformed and Annealed
- Saint-Gobain CHR® K109 Polyimide Film Backing Acrylic Adhesive Pressure Sensitive Tape
- SABIC Innovative Plastics LNP Thermocomp OC004 PPS - Linear (Europe-Africa-Middle East)
- Braskem TN2005 EVA General Film Copolymer
- Akro-Plastic Akromid® B3 GF 35 (2473) PA 6 Dry, 35% Glass Filled
- Arlon 41570R015 0.015" Uncured, Unsupported Silicone Rubber on Release Carrier
Copyright © lookpolymers.com All Rights Reserved