Latrobe HS-29XLâ„¢ ASTM M2-HC High Speed Steel
| Category | Metal , Ferrous Metal , Alloy Steel , Carbon Steel , High Carbon Steel , Tool Steel |
| Manufacturer | Latrobe Steel |
| Trade Name | HS-29XL™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Latrobe HS-29XLâ„¢ ASTM M2-HC High Speed Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
HS-29XL (M2-HC) is the M2 composition with the carbon content increased and with the addition of alloy sulfides. The higher carbon content provides higher hardness and
superior red hardness compared to standard-carbon M2. The alloy sulfides improve machinability and grindability and make it possible to produce accurately-machined tools
without grinding after hardening. Because of the increased carbon content and higher attainable hardness, HS-29XL exhibits abrasion resistance that is similar to M3-1 high
speed steel.Information Provided by Timken Latrobe Steel.Timken sold Latrobe in December 2006. They are now Latrobe Specialty Steels Co.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 8.14 g/cc | 8.14 g/cc | |
| Density | 8.14 g/cc | 0.294 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell C | 65.2 | 65.2 | Oil Quenched from 1218°C |
| 65.6 | 65.6 | Oil Quenched from 1177°C | |
| 65.8 | 65.8 | Oil Quenched from 1149°C | |
| Modulus of Elasticity | 207 GPa | 30000 ksi | |
| Machinability | 50 - 60 % | 50 - 60 % | 1% Carbon Steel |
| Izod Impact Unnotched | 29.8 J | 22.0 ft-lb | Oil Quenched at 1177°C; 520°C Temper Temperature |
| 30.5 J | 22.5 ft-lb | Oil Quenched at 1204°C; 580°C Temper Temperature | |
| 30.5 J | 22.5 ft-lb | Oil Quenched at 1204°C; 650°C Temper Temperature | |
| 32.5 J | 24.0 ft-lb | Oil Quenched at 1204°C; 482°C Temper Temperature | |
| 37.3 J | 27.5 ft-lb | Oil Quenched at 1177°C; 650°C Temper Temperature | |
| 43.4 J | 32.0 ft-lb | Oil Quenched at 1177°C; 482°C Temper Temperature |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.95 µm/m-°C @Temperature 21.0 - 204 °C |
6.083 µin/in-°F @Temperature 69.8 - 399 °F |
|
| 12.54 µm/m-°C @Temperature 21.0 - 358 °C |
6.967 µin/in-°F @Temperature 69.8 - 676 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.98 % | 0.98 % | |
| Chromium, Cr | 4.15 % | 4.15 % | |
| Iron, Fe | 81.29 % | 81.29 % | |
| Manganese, Mn | 0.28 % | 0.28 % | |
| Molybdenum, Mo | 5.0 % | 5.0 % | |
| Silicon, Si | 0.30 % | 0.30 % | |
| Tungsten, W | 6.15 % | 6.15 % | |
| Vanadium, V | 1.85 % | 1.85 % |
| Chemical Properties | Metric | English | Comments |
|---|---|---|---|
| Critical Temperature | 830 °C | 1530 °F | Ac1 |
Users viewing this material also viewed the following:
- PolyOne Lubri-Tech™ AS-20GF/05T Acrylonitrile Butadiene Styrene (ABS), Glass Filled, PTFE Lubricated (discont
- Saint-Gobain CHR® 2285-2 Extruded PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
- Unifrax Insulfrax® S Blanket Insulation
- A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT
- Dymax 930 Coil Terminating, Tamper proofing and Structural Electronic Bonder
- Abatron AboCast/AboCure 8110-3 Flexible Epoxy
- Arlon Thermabond® 99720W015 0.015" Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
- BASF Ultramid® 8253 PA6 (Dry)
- Austin Novel Materials Texalan® 590A Polyether-based TPU
- Arkema Group OREVAC® 9309 EVA Terpolymer
Copyright © lookpolymers.com All Rights Reserved