MRC Polymers NAXELLâ„¢ PC110-919 General Purpose Polycarbonate, Medium High MFR

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer MRC Polymers
Trade Name NAXELL™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF MRC Polymers NAXELLâ„¢ PC110-919 General Purpose Polycarbonate, Medium High MFR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polycarbonate for colorable productsMFR can be modified between 10 to 40 g/10minCan be UV stabilizedInternal and external lubricant can be addedCan be clear to color matchedNot for products that require stringent visual specificationFR package can be addedInformation provided by MRC Polymers Inc.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
solid; ASTM D792
Water Absorption 0.15 %

@Temperature 22.8 °C,
Time 86400 sec
 0.15 %

@Temperature 73.0 °F,
Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.17 mm
 0.0050 - 0.0070 in/in

@Thickness 0.125 in
 ASTM D955
Melt Flow 15 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 15 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 nominal; ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 62.1 MPa

@Thickness 3.17 mm,
Temperature 22.8 °C
 9000 psi

@Thickness 0.125 in,
Temperature 73.0 °F
 ASTM D638
Elongation at Break 60 %

@Thickness 3.17 mm,
Temperature 22.8 °C
 60 %

@Thickness 0.125 in,
Temperature 73.0 °F
 ASTM D638
Flexural Strength 96.5 MPa

@Thickness 3.17 mm,
Temperature 22.8 °C
 14000 psi

@Thickness 0.125 in,
Temperature 73.0 °F
 ASTM D790
Flexural Modulus 2.34 GPa

@Thickness 3.17 mm,
Temperature 22.8 °C
 340 ksi

@Thickness 0.125 in,
Temperature 73.0 °F
 ASTM D790
Izod Impact, Notched 8.54 J/cm

@Thickness 3.17 mm,
Temperature 22.8 °C
 16.0 ft-lb/in

@Thickness 0.125 in,
Temperature 73.0 °F
 ASTM D256
Dart Drop, Total Energy 61.0 J

@Thickness 3.17 mm,
Temperature 22.8 °C
 45.0 ft-lb

@Thickness 0.125 in,
Temperature 73.0 °F
 7.5MPH; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear 68.0 µm/m-°C

@Temperature -40.0 - 35.0 °C
 37.8 µin/in-°F

@Temperature -40.0 - 95.0 °F
 ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 135 °C

@Thickness 3.17 mm
 275 °F

@Thickness 0.125 in
 un-annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 125 °C

@Thickness 3.17 mm
 257 °F

@Thickness 0.125 in
 un-annealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 254 - 271 °C
490 - 520 °F
Middle Barrel Temperature 266 - 282 °C
510 - 540 °F
Front Barrel Temperature 277 - 293 °C
530 - 560 °F
Nozzle Temperature 277 - 293 °C
530 - 560 °F
Melt Temperature 271 - 293 °C
520 - 560 °F
Mold Temperature 48.9 - 93.3 °C
120 - 200 °F
Drying Temperature 116 °C
240 °F
Dry Time 3 - 4 hour
3 - 4 hour
Moisture Content <= 0.020 %
<= 0.020 %
Dew Point <= -17.8 °C
<= 0.000 °F
Drying Air Flow Rate 22.7 - 28.3 l/min
0.800 - 1.00 ft³/min (CFM)
per lb/hour resin processed
Injection Pressure 68.9 - 138 MPa
10000 - 20000 psi
Back Pressure 0.345 - 1.21 MPa
50.0 - 175 psi
Cushion 0.635 cm
0.250 in
Screw Speed 50 - 75 rpm
50 - 75 rpm
Descriptive Properties Value Comments
Fill Rate Moderate
Hold Pressure 40-60% of injection pressure
Packing Pressure 50-75% of injection pressure