BASF Ultramid® FRee A3U40G5 25% Glass Filled PA66 FR (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® FRee A3U40G5 25% Glass Filled PA66 FR (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Flame retardant without halogens and red phosphorus, 25% glass fiber reinforced injection-molding grade; light colorable; outstanding mechanical and electrical properties.Information provided by BASF
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 4.0 - 4.6 %
4.0 - 4.6 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 1.1 - 1.5 %
1.1 - 1.5 %
23°C; 50% RH; ISO 62
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
restricted
Melt Flow 42.6 g/10 min

@Load 5.00 kg,
Temperature 275 °C
42.6 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 140 MPa
20300 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 3.8 %
3.8 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 7.40 GPa
1070 ksi
ISO 527-1/-2
Flexural Strength 160 MPa
23200 psi
at max force; ISO 178
Flexural Modulus 7.40 GPa
1070 ksi
ISO 178
Izod Impact, Notched (ISO) 9.00 kJ/m²

@Temperature 23.0 °C
4.28 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Charpy Impact Unnotched 6.00 J/cm²

@Temperature 23.0 °C
28.6 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 260 °C
500 °F
DIN 53765
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+11 ohm-cm
1.00e+11 ohm-cm
IEC 60093
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
IEC 60093
Dielectric Constant 4.6

@Frequency 1.00 Hz
4.6

@Frequency 1.00 Hz
IEC 60250
Dissipation Factor 0.10

@Frequency 1.00e+6 Hz
0.10

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 280 - 300 °C
536 - 572 °F
Injection-molding/Extrusion
Mold Temperature 80.0 - 90.0 °C
176 - 194 °F
Injection-molding
Descriptive Properties Value Comments
Commercial Status Europe