MRC Polymers MAXTELâ„¢ 600T25 TPO, 25% Talc Filled
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) |
| Manufacturer | MRC Polymers |
| Trade Name | MAXTEL™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | MRC Polymers MAXTELâ„¢ 600T25 TPO, 25% Talc Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
For automotive exterior applicationsExcellent process ability and dimensional stabilityCan be UV StabilizedInternal and external lubricants can be addedInformation provided by MRC Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ISO 1183 |
| Filler Content | 25 % | 25 % | ISO 3451A |
| Linear Mold Shrinkage | 0.010 - 0.016 cm/cm | 0.010 - 0.016 in/in | ISO 294 |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 230 °C |
14 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 59 | 59 | 15sec dwell; ISO 868 |
| Tensile Strength, Yield | 15.00 MPa | 2175 psi | ISO 527 |
| Flexural Strength | 22.99 MPa | 3335 psi | ISO 178 |
| Flexural Modulus | 1.31 GPa | 190 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C @Thickness 3.17 mm |
167 °F @Thickness 0.125 in |
un-annealed; ISO 75 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 182 - 204 °C | 360 - 400 °F | |
| Middle Barrel Temperature | 193 - 216 °C | 380 - 420 °F | |
| Front Barrel Temperature | 204 - 227 °C | 400 - 440 °F | |
| Nozzle Temperature | 216 - 238 °C | 420 - 460 °F | |
| Melt Temperature | 221 - 243 °C | 430 - 470 °F | |
| Mold Temperature | 21.1 - 32.2 °C | 70.0 - 90.0 °F | |
| Drying Temperature | 48.9 - 65.6 °C | 120 - 150 °F | Usually not required |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Injection Pressure | 48.3 - 55.2 MPa | 7000 - 8000 psi | |
| Back Pressure | 0.000 - 1.03 MPa | 0.000 - 150 psi | |
| Cushion | 0.635 cm | 0.250 in |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Fill Rate | Slow to Moderate | |
| Screw Speed | Slow to Moderate |
Users viewing this material also viewed the following:
- MV Labs PR500 PrF3 Praseodymium fluoride
- Ovation Polymers Nima™ HL 18400 HDPE
- Wellman Wellamid® MRGF1475 BK01 20% Mineral/Glass Reinforced Nylon 66
- DuPont Teijin Films Mylar® LB Polyester Film, 48 Gauge (12 µm)
- Fainplast Compounds ART 0699 Rigid PVC, Atoxic for General Purpose
- BNZ Materials PA 26 Insulating Firebrick
- Azdel SuperLite® SL550900-100 PP Resin Matrix / 55% Glass Fiber (2.5 mm Molded Thickness)
- Asia International Enterprise (Hong Kong) 60G8-43GF Nylon 66, 43% Filled
- Gouda Vuurvast LP 85 KP Dense Refractory Brick
- DuPont Performance Polymers Hypalon® 20 Chlorosulfonated Polyethylene Rubber, Gum Compound (discontinued **)&
Copyright © lookpolymers.com All Rights Reserved