| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) |
| Manufacturer | MRC Polymers |
| Trade Name | MAXTEL™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | MRC Polymers MAXTELâ„¢ 600 GF20 TPO, 20% Glass Fiber Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
For automotive exterior applications. Excellent process ability and dimensional stability.Internal and external lubricants can be addedCan be UV StabilizedInformation provided by MRC Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Filler Content | 20 % | 20 % | ASTM D5630 |
| Melt Flow | 9.0 g/10 min | 9.0 g/10 min | ASTM D256 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
| Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790 |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C @Thickness 3.17 mm |
302 °F @Thickness 0.125 in |
un-annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 3.17 mm |
266 °F @Thickness 0.125 in |
un-annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 - 227 °C | 410 - 440 °F | |
| Middle Barrel Temperature | 210 - 227 °C | 410 - 440 °F | |
| Front Barrel Temperature | 210 - 227 °C | 410 - 440 °F | |
| Nozzle Temperature | 210 - 227 °C | 410 - 440 °F | |
| Melt Temperature | 221 - 260 °C | 430 - 500 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 4 hour | 4 hour | |
| Dew Point | <= -17.8 °C | <= 0.000 °F | |
| Drying Air Flow Rate | 22.7 - 28.3 l/min | 0.800 - 1.00 ft³/min (CFM) | per lb/hour resin processed |
| Injection Pressure | 68.9 - 138 MPa | 10000 - 20000 psi | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Cushion | 0.330 - 0.635 cm | 0.130 - 0.250 in | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Fill Rate | Slow to Moderate | |
| Hold Pressure | 40-60% of injection pressure | |
| Packing Pressure | 50-75% of injection pressure |
Users viewing this material also viewed the following:
- NeXolve Clear Optionox® Polyimide Film/Coating
- Lehmann & Voss LUVOCOM® 50/CF/15/TF/15/SI/2/BK-HB Polycarbonate, with carbon fiber, PTFE, lubricant modified
- H.C. Starck Amperit® 583.054 Chromium Carbide-Nickel 83-17 (Cr3C2-Ni)
- Momentive Performance Materials TSE 2297 Heat Cured Rubber - High Duro Translucent
- Tra-Con Tra-Bond FS163 Medium Viscosity Epoxy/Polyamide Adhesive
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 0.50 PHR Zinc Stearate
- CP-Polymer-Technik Wellamid® 6000 MRGV 20/10 HWCP 20% Mineral and 10% Glass Fiber Nylon 6, Heat Stabilized, Conditioned
- Chosun Refractories ALB-65I Special Casting Block
- Solvay Specialty Polymers Ixef® 2530/X9027 Polyarylamide, 55% Mineral + Glass Fiber, DAM (discontinued **)<
- Braskem HB0454 HDPE Blow Molding Polyethylene Copolymer
Copyright © lookpolymers.com All Rights Reserved