PolyOne Lubri-Tech™ NI-30CF/10T-2S Nylon 6/10, Carbon Fiber Reinforced, PTFE/Silicone Lubricated (discontinue
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ NI-30CF/10T-2S Nylon 6/10, Carbon Fiber Reinforced, PTFE/Silicone Lubricated
(discontinue.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Carbon Fiber ReinforcedPTFE/Silicone LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0015 cm/cm | 0.0010 - 0.0015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 186 MPa | 27000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 11.7 GPa | 1700 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 228 MPa | 33000 psi | ASTM D790 |
| Flexural Modulus | 11.7 GPa | 1700 ksi | ASTM D790 |
| Izod Impact, Notched | 2.40 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
4.50 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 100 - 10000 ohm-cm | 100 - 10000 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 249 - 282 °C | 480 - 540 °F | Molding |
| Mold Temperature | 93.3 - 104 °C | 200 - 220 °F | |
| Drying Temperature | 93.3 - 104 °C | 200 - 220 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- GEHR Plastics ECOGEHR® PA 6.10 Nylon 6.10 Dry, 60% Sebacic Acid
- Taiwan PU Corporation TPU-EH80 High Hydrolysis Resistance, Extrusion Molding Polyether Base TPU
- SABIC Innovative Plastics LNP Thermocomp KF003 Acetal Copoly (Asia Pacific)
- Master Bond LED401LV One Component, Moderate Viscosity LED Curable System
- China Tungsten YG8 Tungsten Carbide for Dies and Wear Part Making
- BASF Ultramid® A3Z PA66 (Conditioned)
- Ashley Polymers Ashlene® 126WO PBT Polyester, 30% Glass Reinforced
- Polykemi AB POLYfill PPH T8030 Polypropylene Homopolymer, Mineral Reinforced
- ExxonMobil LD 206.48 Extrusion Coating Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved