BASF Ultramid® B3L BK00464 PA6 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B3L BK00464 PA6 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Impact-modified, free-flowing and rapidly processable injection-molding grade for dry impact-resistant technical articles such as, for example, housings, fittings, small parts and wall plugs.Information provided by BASF
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
ISO 1183
Water Absorption 8.5 - 9.5 %
8.5 - 9.5 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 2.1 - 2.9 %
2.1 - 2.9 %
23°C; 50% RH; ISO 62
Linear Mold Shrinkage 0.0065 cm/cm
0.0065 in/in
restricted
Melt Flow 121 g/10 min

@Load 5.00 kg,
Temperature 275 °C
121 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 35.0 MPa
5080 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 18 %
18 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 0.900 GPa
131 ksi
ISO 527-1/-2
Izod Impact, Notched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 180/A
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eA
Tensile Creep Modulus, 1000 hours 550 MPa

@Strain <=0.500 %
79800 psi

@Strain <=0.500 %
ISO 899-1
Thermal Properties Metric English Comments
Specific Heat Capacity 1.50 J/g-°C
0.359 BTU/lb-°F
Thermal Conductivity 0.320 W/m-K
2.22 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 220 °C
428 °F
DIN 53765
Maximum Service Temperature, Air 160 °C
320 °F
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+10 ohm-cm
1.00e+10 ohm-cm
IEC 60093
Surface Resistance 1.00e+10 ohm
1.00e+10 ohm
IEC 60093
Dielectric Constant 6.4

@Frequency 1.00 Hz
6.4

@Frequency 1.00 Hz
IEC 60250
Dissipation Factor 0.24

@Frequency 1.00e+6 Hz
0.24

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 250 - 270 °C
482 - 518 °F
Injection-molding/Extrusion
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Injection-molding
Descriptive Properties Value Comments
Commercial Status Europe