Lehmann & Voss LUVOCOM® 19-7900 Polyamide 46, with carbon fiber and PTFE
| Category | Polymer , Thermoplastic , Nylon , Nylon 46 |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 19-7900 Polyamide 46, with carbon fiber and PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia compared with metal parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Gear parts for automotive appliances, control disks, cams, sliding elements.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 175 MPa | 25400 psi | |
| Elongation at Yield | 1.2 % | 1.2 % | |
| 1.4 % | 1.4 % | flexural | |
| Modulus of Elasticity | 20.0 GPa | 2900 ksi | |
| Flexural Strength | 250 MPa | 36300 psi | |
| Flexural Modulus | 17.0 GPa | 2470 ksi | |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 150 °C | 302 °F | |
| 160 °C | 320 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 290 °C | >= 554 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1000 ohm | <= 1000 ohm | |
| Insulation Resistance | <= 1000 ohm | <= 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 310 °C | 590 °F | mass temp |
| Nozzle Temperature | 280 - 330 °C | 536 - 626 °F | |
| Zone 1 | 285 - 315 °C | 545 - 599 °F | |
| Zone 2 | 305 - 315 °C | 581 - 599 °F | |
| Zone 3 | 305 - 315 °C | 581 - 599 °F | |
| Mold Temperature | 120 - 140 °C | 248 - 284 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 43200 sec |
176 °F @Time 2.00 - 12.0 hour |
Vacuum Dryer |
| 80.0 °C @Time 7200 - 28800 sec |
176 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® V-341 Polybutadiene Prepreg, 7781 E-Glass Reinforced
- Nilit FRIANYL A63 KV40 Nylon 6.6 for injection molding, 40% glass ball reinforced
- Nilit FRIANYL B63 GV15 Nylon 6 for injection molding, 15% glass fiber reinforced
- SABIC Innovative Plastics ULTEM 2100F PEI
- SABIC Innovative Plastics Ultem DH1004F PEI (Asia Pacific)
- Solvay Specialty Polymers Udel® P-1700 LCD Polysulfone (PSU)
- DuPont Teijin Films Melinex® 513P Polyester Film, 650 Gauge
- Arkema Group Pebax® MV 1041 SN 01 Polyether Block Amide (PEBA) (Dry)
- BASF Ultramid® 8233G HS BK-102 33% Glass Filled PA6 (Dry)
- Von Roll Isola IMI Varnish 704 Solventless Polyester Varnish for Electrical Insulation
Copyright © lookpolymers.com All Rights Reserved