SABIC Innovative Plastics LNP STAT-KON RE004MPC PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON RE004MPC PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* RE004MPC is a compound based on Nylon 66 resin containing 20% Milled Carbon Fiber. Added features of this material are: Exceptional Processing, Clean Compound System, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.840 % | 0.840 % | 23°C / 50% RH; ISO 62 |
| 0.840 % | 0.840 % | 50% RH, 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ISO 527 |
| 130 MPa | 18900 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 3.4 % | 3.4 % | Type I, 5 mm/min; ASTM D638 |
| 5.5 % | 5.5 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 13.86 GPa | 2010 ksi | 1 mm/min; ISO 527 |
| 21.81 GPa | 3163 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 168 MPa | 24400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 207 MPa | 30000 psi | ISO 178 | |
| Flexural Modulus | 6.66 GPa | 966 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 9.85 GPa | 1430 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Unnotched | 9.47 J/cm | 17.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 24.2 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 89.7 µm/m-°C @Temperature -30.0 - 30.0 °C |
49.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 250 °C @Thickness 3.20 mm |
482 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 209 °C | 408 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 209 °C @Thickness 3.20 mm |
408 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 3.0 - 5.0 ohm | 3.0 - 5.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- MV Labs LU500 LuF3 Lutetium fluoride
- RheTech Products GC10P200-01 10% Glass Fiber Reinforced Polypropylene Copolymer, Non-UV Stabilized, Chemically Coupled, Black
- SABIC Innovative Plastics Cycolac® EXABS01 ABS
- DuPont Performance Polymers Sorona® FG3015G NC010 Polytrimethylene Terephthalate (PTT) (Unverified Data**
- Indium Corp. Indalloy 54 Bismuth Solder Alloy
- Henkel Turco Ridoline 4355 Cleaner
- DuPont Performance Polymers Delrin® SC699 NC010 Acetal (POM) (Unverified Data**)
- Chisso Z CLEAN® A1 Purging Solution
- Arlon R32390B020 0.020" Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved