Techmer ES Statiblend® PP FR BK
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | Techmer ES |
| Trade Name | Statiblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Statiblend® PP FR BK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFeature: Flame Retardant, Homopolymer and Semi ConductiveUL File Number: E157318Information provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in³ | ASTM D792 |
| Melt Flow | 11 g/10 min @Load 10.0 kg, Temperature 230 °C |
11 g/10 min @Load 22.0 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 92 | 92 | ASTM D785 |
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| Elongation at Yield | 130 % | 130 % | ASTM D638 |
| Flexural Yield Strength | 42.1 MPa | 6100 psi | ASTM D790 |
| Flexural Modulus | 1.31 GPa | 190 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Thickness 3.17 mm |
0.800 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 2.67 J/cm @Thickness 3.17 mm |
5.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 54.0 µm/m-°C | 30.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.7 °C | 188 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PH 49 GF 50 Polypropylene Homopolymer, 50% Glass Fiber
- Haynes Hastelloy® S alloy, weld metal, aged at 649°C (1200°F) for 1000 hours
- Menzolit Menzolit® SMC 0420 Unsaturated Polyester UP
- Mitsui ADMER® SE800 Elastomer Type Polyolefin
- Saint-Gobain Norton® PFA Fluoropolymer Film
- A. Schulman PP 3449-01 Polypropylene Copolymer Polypropylene
- BorsodChem ONGRO CPE 4002 N Chlorinated Polyethylene
- Arkema Group Lacovyl® PA 1384 Vinyl Copolymer
- DuPont Performance Polymers Delrin® 500CL NC010 Acetal Homopolymer (Unverified Data**)
- Axiall 3240 Rigid PVC, Extrusion
Copyright © lookpolymers.com All Rights Reserved