- Lanxess Pocan® KU 2-7241 000000 PBT, 25% Glass Fiber
Lanxess Pocan® KU 2-7241 000000 PBT, 25% Glass Fiber
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant , Polybutylene Terephthalate (PBT), Glass Filled, Impact Modified |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® KU 2-7241 000000 PBT, 25% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT, 25% glass fibers, injection molding, flame retardant, improved impact strengthInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.800 g/cc | 0.0289 lb/in³ | ISO 60 |
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0026 cm/cm | 0.0026 in/in | 150x105x3, 260°C / MT 80°C; 500 bar; ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.0104 cm/cm | 0.0104 in/in | 150x105x3, 260°C / MT 80°C; 500 bar; ISO 2577 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 260 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 500 °F |
ISO 1133-1 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 MPa | 17400 psi | 5 mm/min; ISO 527-1,-2 |
| Elongation at Break | 3.1 % | 3.1 % | 5 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 195 MPa | 28300 psi | 2 mm/min; ISO 178-A |
| Flexural Modulus | 7.80 GPa | 1130 ksi | 2 mm/min; ISO 178-A |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A |
| <= 10.0 kJ/m² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
ISO 180-1A | |
| 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U |
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
16.7 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| Melting Point | 225 °C | 437 °F | 10 °C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1,-2 |
| Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 75-1,-2 |
| Vicat Softening Point | 200 °C | 392 °F | 50 N; 50 °C/h; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
||
| Oxygen Index | 32 % | 32 % | Method A; ISO 4589-2 |
| Shrinkage | 0.0700 % @Temperature 120 °C, Time 14400 sec |
0.0700 % @Temperature 248 °F, Time 4.00 hour |
post-shrinkage, transverse, 150x105x3; ISO 2577 |
| 0.260 % @Temperature 120 °C, Time 14400 sec |
0.260 % @Temperature 248 °F, Time 4.00 hour |
post-shrinkage, 150x105x3; ISO 2577 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 |
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.8 @Frequency 100 Hz |
3.8 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 225 V | 225 V | Solution A; UL 746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection molding; ISO 294 |
| Dry Time | 4.00 - 8.00 hour @Temperature 120 °C |
4.00 - 8.00 hour @Temperature 248 °F |
|
| Moisture Content | 0.00 - 0.020 % | 0.00 - 0.020 % | Karl Fischer test |
Users viewing this material also viewed the following:
- Prodways PLASTCure Model 200 3D Printing Polymer
- Gouda Vuurvast CURAS 90 PF REPAIR Moldable Refractory Material
- Inno-Comp INNOPOL® CS 4-8000 Polypropylene Random Copolymer
- Momentive Performance Materials Siloprenâ„¢ LSR 2630 Liquid Silicone Rubber - Fast Cure / High Tear
- SABIC Innovative Plastics LNP THERMOCOMP ZF006 PPE+PS (Europe-Africa-Middle East)
- Covestro Desmopan® 487 Thermoplastic Polyurethane
- Dow LDPE 526A Low Density Polyethylene, Blown Film Grade
- BCC Products BC 8660E Urethane Elastomer
Copyright © lookpolymers.com All Rights Reserved