Chosun Refractories HACT-180G High Alumina Castables
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories HACT-180G High Alumina Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.006867 - 0.010791 GPa @Temperature 110 °C, Time 86400 sec |
0.9960 - 1.5651 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.006867 - 0.010791 GPa @Temperature 1000 °C, Time 10800 sec |
0.9960 - 1.5651 ksi @Temperature 1830 °F, Time 3.00 hour |
||
| 0.007848 - 0.011772 GPa @Temperature 1350 °C, Time 10800 sec |
1.138 - 1.7074 ksi @Temperature 2460 °F, Time 3.00 hour |
||
| Compressive Strength | 24.5 - 29.4 MPa @Temperature 110 °C, Time 86400 sec |
3560 - 4270 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| 29.4 - 34.3 MPa @Temperature 1000 °C, Time 10800 sec |
4270 - 4980 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 34.3 - 44.1 MPa @Temperature 1350 °C, Time 10800 sec |
4980 - 6400 psi @Temperature 2460 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 1.047 W/m-K @Temperature 260 °C |
7.253 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
| 1.1166 W/m-K @Temperature 540 °C |
7.7369 BTU-in/hr-ft²-°F @Temperature 1000 °F |
||
| 1.1748 W/m-K @Temperature 800 °C |
8.1398 BTU-in/hr-ft²-°F @Temperature 1470 °F |
||
| Maximum Service Temperature, Air | 1800 °C | 3270 °F | limited |
| Shrinkage | -0.250 % @Temperature 1350 °C, Time 10800 sec |
-0.250 % @Temperature 2460 °F, Time 3.00 hour |
|
| -0.0600 % @Temperature 110 °C, Time 86400 sec |
-0.0600 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 92 % | 92 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Spray | |
| Material Required for Estimating(kg/?) | 2,650 |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 51 T 20 Polypropylene Copolymer, 20% Micronized Talc
- Solvay Specialty Polymers Solef® 21508 PVDF Copolymer (discontinued **)
- Solvay Specialty Polymers Algoflon® 25CAR+5CER PTFE; Petroleum Coke and Ceramic Filled (discontinued **)
- A. Schulman POLYFORT™ FPP 1239H Glass Filled Chemically Coupled Homopolymer Polypropylene
- Dow Corning TM-1951 EMULSION
- 3M 1181 EMI Shielding Tape
- Beijing Chemical Industry KAIFA® 201-G30R PBT Resin
- Axiall 6850 Moldings & Extrusions Flexible PVC
- Braskem CP 741 Blow Molding Polypropylene
- SABIC Innovative Plastics LNP LUBRICOMP QCL349 PA6.10
Copyright © lookpolymers.com All Rights Reserved