Lanxess Pocan® B 3216 HR 000000 PBT 16% Glass Fiber

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Pocan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Pocan® B 3216 HR 000000 PBT 16% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT, 16% glass fibers, injection molding, improved impact strength, hydrolysis stabilizedInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.40 g/cc
1.40 g/cc
ISO 1183
Bulk Density 0.700 g/cc
0.0253 lb/in³
ISO 60
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0060 cm/cm
0.0060 in/in
60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0010 cm/cm
0.0010 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.010 cm/cm
0.010 in/in
60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Melt Flow 24 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 24 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 ISO 1133-1
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa
14500 psi
ISO 527-1, -2; 5 mm/min
Elongation at Break 3.7 %
3.7 %
ISO 527-1, -2; 5 mm/min
Tensile Modulus 5.90 GPa
856 ksi
ISO 527-1, -2; 1 mm/min
Flexural Strength 165 MPa

@Strain 4.40 %
 23900 psi

@Strain 4.40 %
 2 mm/min; ISO 178-A
Flexural Yield Strength 160 MPa

@Strain 3.50 %
 23200 psi

@Strain 3.50 %
 2 mm/min; ISO 178-A
Flexural Modulus 5.60 GPa
812 ksi
2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
<= 10.0 kJ/m²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1A
Izod Impact, Unnotched (ISO) 30.0 kJ/m²

@Temperature -30.0 °C
 14.3 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1U
45.0 kJ/m²

@Temperature 23.0 °C
 21.4 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1U
Charpy Impact Unnotched 3.50 J/cm²

@Temperature -30.0 °C
 16.7 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eU
5.00 J/cm²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 22.2 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
CTE, linear, Transverse to Flow 130 µm/m-°C

@Temperature 23.0 - 55.0 °C
 72.2 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
ISO 75-1, -2
Vicat Softening Point 200 °C

@Load 5.10 kg
 392 °F

@Load 11.2 lb
 120°C/hour; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Strength 36.0 kV/mm

@Thickness 1.00 mm
 914 kV/in

@Thickness 0.0394 in
 IEC 60243-1
Comparative Tracking Index 275 V
275 V
d.a.m.; Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 250 - 270 °C
482 - 518 °F
260 °C
500 °F
for test specimens; ISO 294
Mold Temperature 80.0 °C
176 °F
for test specimens; ISO 294
80.0 - 100 °C
176 - 212 °F
Drying Temperature 120 °C
248 °F
Dry Time 4 - 8 hour
4 - 8 hour
Moisture Content 0.00 - 0.020 %
0.00 - 0.020 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 7792-1-PBT, GHMR, 09-050, GF16