SABIC Innovative Plastics LNP KONDUIT PX09322 PA 6 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Konduit |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP KONDUIT PX09322 PA 6 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
White colored thermally conductive mineral filled PA6 FR compound
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0058 cm/cm | 0.0058 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0053 cm/cm | 0.0053 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 0.80 % | 0.80 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 10.42 GPa | 1511 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 81.0 MPa | 11700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 80.0 MPa | 11600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 10.96 GPa | 1590 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.220 J/cm | 0.412 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.31 J/cm | 2.45 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 36.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Thermal Conductivity | 0.860 W/m-K | 5.97 BTU-in/hr-ft²-°F | through-plane, ø80*3mm discs; ISO 22007-2 |
| 1.50 W/m-K | 10.4 BTU-in/hr-ft²-°F | through-plane, 10*10*3mm sample; ASTM E 1461-07 | |
| 2.68 W/m-K | 18.6 BTU-in/hr-ft²-°F | in-plane, ø80*3mm discs; ISO 22007-2 | |
| 6.00 W/m-K | 41.6 BTU-in/hr-ft²-°F | in-plane, ø25*0.4mm disc; ASTM E 1461-07 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C @Thickness 6.40 mm |
410 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 182 °C @Thickness 6.40 mm |
360 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.20 mm |
V-0 @Thickness 0.0472 in |
UL 94 |
| Glow Wire Test | 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 8.10e+14 ohm | 8.10e+14 ohm | ASTM D257 |
| Comparative Tracking Index | >= 600 V | >= 600 V | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Water Immersion, Start F1 from 1mm onward | PASSES | UL 746C |
| PASSES | UL 746C |
Users viewing this material also viewed the following:
- Network Polymers F7000 Polystyrene
- PolyOne Dynaflex™ G7702-9001-02 Thermoplastic Elastomer (TPE)
- Ineos H20A-00 Polypropylene Homopolymer
- TIMCAL TIMREX® LSG 44 Natural Graphite Flakes
- A. Schulman POLYBATCH™ Brown 10306 Concentrate Based In Polyethylene
- Hexcel® HexWeb® CR III 5/32-5052-.0025 Corrosion Resistant Specification Grade Aluminum Honeycomb
- EDRO UltraChem® #15 Precipitation Hardening Stainless Mold Steel
- China-Yixing Longly Refractories Shelf Corundum-Mullite
- DuPont Performance Polymers Neoprene FB Polychloroprene Rubber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved