Kolon KOPA® KN333G35CRBK G/F Reinforced Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Kolon |
| Trade Name | Kopa® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOPA® KN333G35CRBK G/F Reinforced Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
EG-resistant, high strength, dimensionally stableApplications Coolant temperature control partsInformation provided by API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.40 % | 0.40 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength | 186 MPa | 27000 psi | ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | ASTM D638 |
| Flexural Strength | 294 MPa | 42600 psi | ASTM D790 |
| Flexural Modulus | 8.826 GPa | 1280 ksi | ASTM D790 |
| Izod Impact, Notched | 1.08 J/cm | 2.02 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 µm/m-°C | 11.1 µin/in-°F | ASTM D696 |
| Melting Point | 255 °C | 491 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.6 | 3.6 | ASTM D150 |
| Dielectric Strength | 21.0 kV/mm | 533 kV/in | ASTM D149 |
| Arc Resistance | 135 sec | 135 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Shin-Etsu Silicones KE-3421 Silicone, RTV Conformal Coating
- A. Schulman FORMION™ FI 335 Ionomer
- Epoxy Technology EPO-TEK® M10-D Epoxy Paste
- BASF Novolen® 1102 G Polypropylene
- BASF Ultramid® A3HG7 BK 00564 35% Glass Filled PA66 (Dry)
- Arlon 41580R030 0.030" Uncured, Unsupported Silicone Rubber on Release Carrier
- Adell BW-17 Nylon 6, 35% Glass Reinforced; Superior Finish
- Techmer ES HiFill® PA4/6 GF5 HS 5% Glass Filled
Copyright © lookpolymers.com All Rights Reserved